The diploma thesis is related to the preparation of hydroxyapatite complex structures by additive manufacturing known as Lithography based ceramics manufacturing – LCM. A photosensitive suspension containing hydroxyapatite particles was used for 3D printing of ceramic complex structures. The influence of printing parameters on the resulting macrostructure, microstructure, density, and dimensional accuracy was evaluated. The aim was to obtain ceramic components without delamination of the layers and optimise following post-processing steps (cleaning and thermal treatment). It was found that the exposure time has a significant effect on the dimensional accuracy of printed parts. During observation microstructure of printed parts, a microporosity at the interface of printed layers, which can cause delamination of several layers was identified. High-temperature dilatometry showed different temperature of beginning densification process in the longitudinal and perpendicular directions to the layers. That could be an initiation mechanism for delamination of the layers. X-ray diffraction analysis determined a single-phase composition of powder in photosensitive suspension and sintered parts. A commercial product LithaSol 20 was suggested as a suitable cleaning agent and efficiency of the ultrasound field for cleaning was demonstrated. Based on the thermogravimetric analysis an optimized cycle of heat treatment was designed. The optimisation led to time saving (49 hours), while maintaining density, dimensional accuracy and macrostructure of the 3D printed structures.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:442598 |
| Date | January 2021 |
| Creators | Valenová, Ludmila |
| Contributors | Hadraba, Hynek, Drdlík, Daniel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds