In the oxidative refining of metallurgical grade silicon the loss of Si to the slag in the form of SiO2 is an economical concern. The purpose of this report is to investigate the possibility of using SiO2 and mechanical stirring to remove Ca and Al as a substitute to the oxidative refining. In the experiments graphite crucibles were used in a vertical resistance furnace and controlled argon atmosphere. The removal rate of Ca and Al are measured by X-ray fluorescence and the slag is examined in a scanning electron microscope. The slag formation kinetics are examined and a calculation of the activities of Ca, Al and their respective oxides in the slag phase is conducted. The driving forces of creating CaO and Al2O3 in this system is calculated to better understand the behavior of the Ca and Al removal. The results show that removal of dissolved Ca and Al by mechanical stirring is possible and in this setup a stirring time of 20 minutes is sufficient since no more refining can be obtained by increasing it.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-170442 |
| Date | January 2015 |
| Creators | Sandell, Mikael |
| Publisher | KTH, Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds