The application of struvite (magnesium ammonium phosphate,!MgNH&PO& ∙ 6H+O)
precipitation and its recycling use for the purpose of ammonia removal from both
synthetic solutions and landfill leachate were investigated in this study. The results
demonstrated that chemical precipitation by struvite formation is efficient for ammonia
removal from aqueous solutions. In addition, by recycling the thermal residue of struvite,
continuously removing ammonia can technically be achieved.
In the struvite precipitation, ammonia removal significantly depended on the pH and
chemical molar ratios of NH&
,:!Mg+,:!PO& ./. For synthetic solution (TAN=1,000 mg/L),
remarkable TAN removal efficiency of over 98% has been reported when the molar ratio
of NH&
,:!Mg+,:!PO& ./ equals 1.0:1.2:1.2, 1.0:1.3:1.3, 1.0:1.3:1.4 and 1.0:1.5:1.5 at
optimum pH 9. The optimum combinations of reagents applied in landfill leachate
(TAN=1,878 mg/L) were!NH&
,:!Mg+,:!PO& ./ =1.0:1.3:1.3, 1.0:1.4:1.3, 1.0:1.5:1.4 and
1.0:1.5:1.5 at optimum pH 9.5, all of which displayed excellent TAN removal
efficiencies of over 99%. Response surface method (RSM) helped to analyze the data and
optimize the results.
The struvite pyrolysate provided best performance of removing ammonia in both
simulated wastewater and landfill leachate at a dosage of 60 g/L, when struvite was
previously heated at 105 by oven for 2.5 h. In the recycling phase, the struvite
pyrolysate resulting from NaOH-mediated pyrolysis was more effective at continuously
treating ammonia synthetic solution than was direct heating, with an initial mode of
87.4% at the beginning to 75.1% in the fifth round and direct heating of struvite from
80.9% in the first cycle and 60.6% in the final cycle. The struvite pyrolysate formed by
NaOH-mediated pyrolysis performed with greater ability to continuously eliminate
ammonia from landfill leachate (97.2% removal at the beginning and 72.3% in the fifth
round), than did directly heated struvite (98.4% in the first cycle and 81.3% in the final
cycle). Additionally, microwave irradiation could also dissociate struvite, which
subsequently demonstrated moderate TAN removal in recycling phases.
Identifer | oai:union.ndltd.org:uottawa.ca/oai:ruor.uottawa.ca:10393/34492 |
Date | January 2016 |
Creators | Zhang, Chi |
Contributors | Sartaj, Majid |
Publisher | Université d'Ottawa / University of Ottawa |
Source Sets | Université d’Ottawa |
Language | English |
Detected Language | English |
Type | Thesis |
Page generated in 0.0018 seconds