Electrochemical double layer capacitors (EDLCs, also called supercapacitors or ultracapacitors) are high power density energy storage devices that operate through the separation of charge at the electrochemical interface between an electrode and a supporting electrolyte. Numerous types of carbon materials with high surface area and internal porosity, such as activated carbon, carbon fabrics, nanotubes, and reduced graphene oxide have been studied as electrode materials. Electrolytes such as aqueous alkaline and acid solutions usually give high capacitance, while organic and ionic liquids provide a wider operation voltage.
Graphene, due to its high theoretical surface area of 2630 m2/g, good electrical conductivity, and relatively low density, is being studied as an electrode material in EDLCs. The objective of this dissertation is thus to study effective methods for synthesis
of graphene-based materials, and to investigate their behavior in EDLCs. This work explored microwave assisted synthesis of graphite oxide (‘MEGO’, prepared in less than one minute by irradiation of graphite oxide by microwave). This material was further chemically activated to obtain a unique carbon material, activated microwave exfoliated graphite oxide (‘a-MEGO’) with specific surface areas up to 3100 m2/g. Gas adsorption measurements were used to study the specific surface area and porosity of a set of a-MEGO samples, which were also studied by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) for their structure, and by combustion analysis (i.e., elemental analysis) and X-ray photoelectron spectroscopy (XPS) to understand their elemental composition. Cyclic voltammetry (CV), galvanostatic charge/discharge, and frequency response, tests were done in order to study the performance of these new carbon materials as electrodes in both aqueous and organic electrolytes in a two electrode cell set up. / text
| Identifer | oai:union.ndltd.org:UTEXAS/oai:repositories.lib.utexas.edu:2152/ETD-UT-2012-12-6576 |
| Date | 01 February 2013 |
| Creators | Murali, Shanthi |
| Source Sets | University of Texas |
| Language | English |
| Detected Language | English |
| Type | thesis |
| Format | application/pdf |
Page generated in 0.0023 seconds