The Y₁Ba₂Cu₃0x superconducting thin films were made by both sequential electron-beam evaporation and co-evaporation of Cu, BaF₂ and Y, followed with high temperature post-deposition annealing.
The possibility of making Y₁Ba₂Cu₃0x superconducting film in situ with BaF₂ as the Ba source was investigated by studying the conditions of in situ conversion of BaF₂ to BaO. The BaO concentration in the film as function of the substrate temperature was estimated with an equilibrium thermodynamic model and found to agree with the experimental results.
A brief experimental and theoretical exploration of BaCl₂ also showed that BaCl₂ does not have any advantage over BaF2 as the Ba source for in situ growth of Y-Ba-Cu-0 films from the growth temperature point of view. / Science, Faculty of / Physics and Astronomy, Department of / Graduate
| Identifer | oai:union.ndltd.org:UBC/oai:circle.library.ubc.ca:2429/28987 |
| Date | January 1990 |
| Creators | Gao, Yuan |
| Publisher | University of British Columbia |
| Source Sets | University of British Columbia |
| Language | English |
| Detected Language | English |
| Type | Text, Thesis/Dissertation |
| Rights | For non-commercial purposes only, such as research, private study and education. Additional conditions apply, see Terms of Use https://open.library.ubc.ca/terms_of_use. |
Page generated in 0.0014 seconds