Orientador: Monica Campos Serra / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T21:21:31Z (GMT). No. of bitstreams: 1
Magalhaes_ClaudiaSilamide_D.pdf: 3601451 bytes, checksum: 40e0276b094752f2e3dcbfd845829566 (MD5)
Previous issue date: 2000 / Resumo: Este estudo teve como objetivo avaliar a rugosidade superficial de duas resinas modificadas por poliácidos e de um ionômero de vidro modificado por resina, submetidos a doistrattmrentos superfzciais de acabamento e polimento, em função do tempo, através de um modelo experimental in situo Vinte voluntários utilizaram, durante 28 dias cansecutivos, dispositivos acrz1icos intra-bucais, contendo corpos-de-proVQ confeccionados com um ionômero de vidro modificado por resina - Fuji 11 LC lmproved (aC) e com duas resinas compostas modificadas por poliácidos - Compoglass F (Vivadent) e Dyract AP (Dentsply I DeTrey). Os corpos-de-prova de dimens&s padronizadas (n=20) foram submetidos a acabamento e polimento com um sistema de discos de lixa a base de óxido de alumínio (Sof-Lex - 3M) ou com pontas de resina impregnadas com éxido de alumínio (Enhance - Dentsply). O grupo controle não recebeu acabamento e polimento, sendo apenas polimerizado contra a superjIcie de uma tira de matriz de poliéster. A cada voluntário foi fornecido o mesmo tipo de escova dental e dentifrício, além de instruç1Jes especifzcas sohre a utilização e higieniz(Jfâo do dispositivo intra-hucal. A rugosidade superficial dos materiais foi quantificada através da medida da rugosidade média (RcJ de nove segmentos lineares predeterminad()s de cada c()rpo-de-pr()va, imediatamente após os procedimentos de acabamento e polimento (/'.0) e após 1 (1'J), 2(1'2), 3(1'3), 7(1'7), 14(1'14), 21 (l'21) e 28 (l' 28) dias de permanência no meio bucal. Para cada tempo estudado foi realizada uma análise .de covariância, considerando T{) como covariáveL Foram aplicadas a decomposição de soma de quadrados e a diferença mínima significativa de Tukey para estudar as interações signifzcativas e as comparações pareadas, ao nível de signiflCância de 5%. Os resultados foram significativos para o efeito da interação Material x Tratamento, exceto no T 28. Inicialmente, para os materiais Compoglass F e Dyract AP, o tratamento com Sof-Lex promoveu maior lisura superficial que Enhance. Os tratamentos com Sof-Lex e Enhance não .cliferiram entre si e aumentaram a rugosidade superficial de Fuji II LC Improved em relação ao controle. A() término da perÍOlJ() de ()bservaÇÕ(), ()S materiais híbridas de ionômer() de vidr() e resina composta submetidos a acabamento e polimento apresentaram rugosidade superficial semelhante ao controle, a despeit() da técnica utilizada / Abstract: The purpose of this study was to evaluate the surface roughness of two polyacid modified composite resins and a resin modified glass-ionomer submitted to two finishing and polishing treatments, as afunction oftime, using an in situ experimental modelo A resin modified glassionomer Fuji II LC lmproved (GC) and two polyacid modified composite resins Compoglass F (Vivadent) and Dyract AP (Dentsply / DeTrey) were analyzed. Cylindrical specimens with standardized dimensions were made using each material (n= 20). Surface treatments were erformed with Sof-Lex (3M) discs or Enhance (Dentsply) tips. Specimens of control groups were not submitted to surface treatments. Twenty volunteers ware palatal appliances in which nine specimens were flXed, during 28 days. The same kind of toothbrush and dentifrice were supplied to each volunteer. Standardized brushing technique was directed to them in order to clean the appliances up. Average surface roughness (Ra) was measured with a roughness tester (Surfcorder SE 1700) immediatelyafter the treatment (1'0) and after 1 (1'1), 2 (1'2),3(1'3), 7 (1'7J, 14 (1'14), 21 (1'21), 28 (1'28) days, under oral conditions. Nine readingsfor each specimen were averaged to give a single value. Data were submitted to Analysis of ovariance considering To values the covariate. Sums of squares decompositions followed by Tukey's Least-significant difference were used to study significative interactions and pairwise comparisons, at 5% significance levei. There was statistically significant effect of interaction Material X Treatment at each time period, excepted T28. lnitially, specimens of materiais Compoglass F and Dyract AP treated with Sof-Lex were smoother than which were treated with Enhance. There was not statistically significant difference between treatments with SofLex and Enhance for Fuji 11 LC lmproved, but both increased its roughness, comparing to controlo After the exposed time to the oral conditions, it was possible to conclude that glassionomer composite resin hybrid materiais finished and polished surfaces presented roughness that was similar to untreated ones, regardless of the polishing method / Doutorado / Dentística / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288316 |
| Date | 18 February 2000 |
| Creators | Magalhães, Claudia Silami de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Serra, Mônica Campos, 1964-, Candido, Maria Salete Machado, Junior, Walter Gomes Miranda, Jansen, Wellington Correa, Pimenta, Luiz Andre Freire |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 114p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0089 seconds