The use of hydrophobic surfaces is important for many processes both in nature and industry. Interactions between hydrophobic species play a key role in industrial applications such as water-cleaning procedures and pitch control during papermaking but they also give information on how to design surfaces like hydrophobic mineral pigments. In this thesis, the influence of surface properties on wetting and interaction forces has been studied. Surfaces with close-packed particles, pore arrays, randomly deposited nanoparticles as well as reference surfaces were prepared. The atomic force microscope (AFM) was utilized for force and friction measurements while contact angles and confocal Raman microscopy experiments were mainly used for wetting studies. The deposition of silica particles in the size range of nano- to micrometers using the Langmuir-Blodgett (LB) technique resulted in particle coated surfaces exhibiting hexagonal close-packing and close to Wenzel state wetting after hydrophobization. Force measurements displayed long-range interaction forces assigned to be a consequence of air cavitation. Smaller roughness features provided larger forces and interaction distances interpreted as being due to fewer restrictions of capillary growth. Friction measurements proved both the surface structure and chemistry to be important for the observed forces. On hydrophobic pore array surfaces, the three-phase contact line of water droplets avoided the pores which created a jagged interface. The influence of the pores was evident in the force curves, both in terms of the shape, in which the three-phase contact line movements around the pores could be detected, as well as the depth of the pores providing different access and amount of air. When water/ethanol mixtures were used, the interactions were concluded to be due to ethanol condensation. Confocal Raman microscopy experiments with water and water/ethanol mixtures on superhydrophobic surfaces gave evidence for water depletion and ethanol/air accumulation close to the surface. Force measurements using superhydrophobic surfaces showed extremely long-range interaction distances. This work has provided evidence for air cavitation between hydrophobic surfaces in aqueous solution. It was also shown that the range and magnitude of interaction forces could, to some extent, be predicted by looking at certain surface features like structure,roughness and the overall length scales. / <p>QC 20121011</p>
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-103409 |
Date | January 2012 |
Creators | Hansson, Petra M |
Publisher | KTH, Yt- och korrosionsvetenskap, Stockholm |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-CHE-Report, 1654-1081 ; 2012:52 |
Page generated in 0.0017 seconds