Previous issue date: 2018-05-28 / Nenhuma / A utilização de materiais cimentícios suplementares (MCS) na produção de cimento é uma estratégia bastante difundida para diminuição de custos de produção, e pode contribuir para a minimização da emissão de CO2. Estes materiais, ao reagirem com o hidróxido de cálcio (CH), gerado na hidratação do cimento, formam silicatos de cálcio e aluminatos de cálcio hidratados adicionais, contribuindo para o ganho de resistência. Segundo a normativa brasileira, para ser considerado um material pozolânico, o somatório de óxidos de Si, Al e Fe deve ser maior do que 70%. No entanto este requisito deve ser tomado com restrições, pois evidências indicam que somente a fração amorfa dos óxidos pozolânicos é que consomem CH. Diante disto, este trabalho teve por objetivo geral avaliar de forma comparativa a influência da composição química e da fração amorfa dos óxidos pozolânicos na reatividade de materiais cimentícios suplementares. Foram estudados uma cinza volante da combustão do carvão (CV); de um resíduo de cerâmica vermelha (RCV); e de um metacaulim (MK). Os materiais tiveram a granulometria ajustada a fim de se obter um D50 de 4 ± 2 µm, buscando uma menor diferença entre a distribuição granulométrica dos MCS e o pó de quartzo (PQ), empregado para compor um padrão secundário de referência, o que permite isolar o fator consumo de cimento nas análises. Os MCS foram caracterizados por FRX, por granulometria à laser, por adsorção de nitrogênio, por picnometria de gás hélio, e microscopia eletrônica de varredura. Empregou-se também DRX em conjunto com o refinamento de Rietveld, utilizando-se o método do padrão interno para a quantificação de fases. A reatividade dos MCS foi medida pelo método de Fratini, por TG/DTG e por resistência à compressão, em pastas e argamassas. Constatou-se que todos os MCS são reativos. O teor de amorfos totais em geral não explica o consumo de CaO, nem as resistências de argamassas. O teor de alumina amorfa apresenta considerável influência sobre consumo de CH, medido em análise térmica, em relação à pasta com PQ. O emprego de pastas para ensaios de resistência, e o padrão com PQ, permitiu avaliar a contribuição da reação dos MCS para as resistências, e, neste caso o teor de amorfos totais e de Al2O3 amorfa apresentam a mesma tendência de comportamento, quanto maior o teor, maior a resistência. No entanto, esta tendência não foi observada quando o teor de SiO2 é isolado, pois o RCV não segue o mesmo comportamento. Foi observado também que o teor elevado de Fe2O3 do RCV pode ser o responsável pela baixa redução de CaO observada no ensaio de Fratini deste MCS. / The use of supplementary cementitious materials (SCM) in the cement production is an usually strategy to reduce costs, and it can promote the reduce of the CO2 emissions. These materials react with the calcium hydroxide (CH), generated in the cement hydration, forming hydrated calcium silicates and aluminates, contributing for the compressive strength. A pozzolanic material has to have, according the Brazilian Standards, a sum of Si, Al and Fe oxides above 70%. However, this requirement have to be taken in account with caution, as evidences indicate that only the amorphous fraction of the pozzolanic oxides consume CH. The aim of this work is to evaluate in a comparative way the influence of the chemical composition and of the amorphous fase of pozzolanic oxides in the reactivity of supplementary cementitious materials. It was studied a fly ash from coal burning (FA), a fired-clay brick powder (FCP) and a comercial metacaulim (MK). The size distribution of the material was adjusted in order to obtain a D50 of 4 ± 2 µm, in order to adjust the granulometry of the materials with the quartz powder (QP), that was employed in a secondary reference composition. The use of this secondary reference allows to compare the pozzolanic materials mixtures with a reference with the same cement consumption. The SCM were characterized by XRF, by laser granulometry, by nitrogen adsorption method, helium gas pycnometry, and by scanning electronic microscopy. It was also employed XRD associated with Rietveld refinement, using the internal pattern method for phase quantifying. The SCM reactivity was measured by Fratini Method, by TG/DTG and by compressive strength, in cement pastes and mortars. It was found that all SCM are reactions. The total amorphous content in general does not explain the CaO consumption, neither the mortars strength. The amorphous alumina content shows a considerable influence on the CH consume measured by TG, taking as reference the pastes with QP. The use of cement paste for compressive strength tests, as well the reference with QP, allowed to evaluate the contribution of the reactivity of SCM for the strength, and, in this case, the total amorphous content and the amorphous Al2O3 content presented the same tendency of behaviour: as big is the content, as big is the strength. However, this tendency it was not observed when the amorphous SiO2 is isolated, because the FCP does not have the same behaviour. It also was observed that the high content of Fe2O3 in the FCP can be responsable for the low tax of CaO consumption observed in the Fratini method of this SCM.
Identifer | oai:union.ndltd.org:IBICT/oai:www.repositorio.jesuita.org.br:UNISINOS/7154 |
Date | 28 May 2018 |
Creators | Fernandes, Ana Júlia Maciel Marinho |
Contributors | http://lattes.cnpq.br/5195306459511343, Brehm, Feliciane Andrade, Kulakowski, Marlova Piva |
Publisher | Universidade do Vale do Rio dos Sinos, Programa de Pós-Graduação em Engenharia Civil, Unisinos, Brasil, Escola Politécnica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UNISINOS, instname:Universidade do Vale do Rio dos Sinos, instacron:UNISINOS |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds