Effect of surface treatments on interfacial strength and durability of metal-polymer composite bond

Effect of surface treatments on Strength and durability of aluminum 6061-Henkel Hysol EA 9891RP (room temperature curing epoxy) bond was studied using single lap shear, flatwise tensile and wedge crack test. The interfacial strength (IFSS) and % cohesive fracture varied with composite adhesive thickness and 0.03-0.04 mm that maximized the interfacial fracture was chosen to compare surface treatments. The effect of treatments on IFSS and tensile strength increased in the following order: PAA+BR127 (RT) < UT+BR127 (120oC) < Alodine < Alodine+EC3901(RT) < Alodine+BR127 (RT) < PAA < UT < UT+BR127 (RT) < Alodine+EC3901 (90oC) < PAA+EC3901(RT) < PAA+EC3901(90oC) < PAA+BR127 (120oC) < UT+EC3901(90oC) < UT+EC3901(RT) < Alodine+BR127 (120oC). The environmental durability decreased in the following order Alodine+EC3901 (90oC) < Alodine+BR127 (120oC) < PAA+BR127 (120oC) < PAA+EC3901 (90oC) < UT < UT+EC3901 (90oC) < UT+EC3901 (RT) < PAA+EC3901 (RT). PAA and Alodine, combined with BR127 (120 oC) and EC3901 (90oC) are the optimal surface treatments / October 2016

Identiferoai:union.ndltd.org:MANITOBA/oai:mspace.lib.umanitoba.ca:1993/31738
Date14 September 2016
CreatorsSumaiya, Syeda Noor E
ContributorsJayaraman, Raghavan (Mechanical Engineering), Wu, Nan (Mechanical Engineering), Liu, Song (Medical Microbiology)
Source SetsUniversity of Manitoba Canada
Detected LanguageEnglish

Page generated in 0.0019 seconds