Effect of surface treatments on Strength and durability of aluminum 6061-Henkel Hysol EA 9891RP (room temperature curing epoxy) bond was studied using single lap shear, flatwise tensile and wedge crack test. The interfacial strength (IFSS) and % cohesive fracture varied with composite adhesive thickness and 0.03-0.04 mm that maximized the interfacial fracture was chosen to compare surface treatments. The effect of treatments on IFSS and tensile strength increased in the following order: PAA+BR127 (RT) < UT+BR127 (120oC) < Alodine < Alodine+EC3901(RT) < Alodine+BR127 (RT) < PAA < UT < UT+BR127 (RT) < Alodine+EC3901 (90oC) < PAA+EC3901(RT) < PAA+EC3901(90oC) < PAA+BR127 (120oC) < UT+EC3901(90oC) < UT+EC3901(RT) < Alodine+BR127 (120oC). The environmental durability decreased in the following order Alodine+EC3901 (90oC) < Alodine+BR127 (120oC) < PAA+BR127 (120oC) < PAA+EC3901 (90oC) < UT < UT+EC3901 (90oC) < UT+EC3901 (RT) < PAA+EC3901 (RT). PAA and Alodine, combined with BR127 (120 oC) and EC3901 (90oC) are the optimal surface treatments / October 2016
| Identifer | oai:union.ndltd.org:MANITOBA/oai:mspace.lib.umanitoba.ca:1993/31738 |
| Date | 14 September 2016 |
| Creators | Sumaiya, Syeda Noor E |
| Contributors | Jayaraman, Raghavan (Mechanical Engineering), Wu, Nan (Mechanical Engineering), Liu, Song (Medical Microbiology) |
| Source Sets | University of Manitoba Canada |
| Detected Language | English |
Page generated in 0.0016 seconds