O objetivo deste estudo foi avaliar pinos pré-fabricados de fibra de vidro (White Post DC/FGM) submetidos à customização por desgaste da porção apical. Experimento 1: 5 pinos n. 4 foram divididos em 5 grupos (G) de acordo com o instrumento de desgaste: GA - sem desgaste, GB- mini torno industrial (Dentsply), GC - ponta diamantada n. 3195F (KG Sorensen), GD - disco de lixa de granulação média (Sof-Lex/3M/ESPE), GE- alicate (Tramontina). Observou-se a micromorfologia dos pinos em microscópio eletrônico de varredura (ZEISS/DSM 960). Experimento 2: 60 pinos de diferentes diâmetros foram divididos em 6 grupos: G0 - pinos n. 0,5, G1 - pinos n. 1, G2 - pinos n. 2, G3 - pinos n. 3, G4 - pinos n.4, G5 - pinos n. 4 com terço apical desgastado com discos de lixa até o equivalente ao terço apical dos pinos n. 2. Os pinos foram submetidos ao teste de flexão de 3 pontos na máquina de ensaios universal (Instron 5500 R), conforme ISO 10477. Experimento 3: 20 caninos humanos permanentes sofreram tratamento endodôntico e remoção das coroas clínicas padronizando 15 mm de remanescente radicular. Os dentes foram incluídos em resina acrílica com simulação do ligamento periodontal, receberam férula de 2 mm e foram divididos em 2 grupos: GI - pinos n. 4 cimentados em condutos preparados com broca equivalente ao pino (FGM), GII - pinos n. 4 customizados no terço apical cimentados em condutos preparados com brocas (FGM) equivalentes aos pinos n. 2 em 10 mm e n. 4 em 5 mm. Os pinos foram cimentados com cimento resinoso (Rely X U100/3M/ESPE), os corpos de prova receberam coroas diretas de resina composta (Enforce Core/Dentsply) padronizadas com coras de policarbonato (TDV) e foram submetidos ao teste de resistência à fratura na Instron a 45da ferramenta cilíndrica, com força de 500 N aplicada a 2 mm da incisal na face palatina/lingual, com velocidade de 0,5 mm/min até falha. O padrão de fratura foi classificado em favorável ou desfavorável. Os resultados foram tratados estatisticamente por teste de análise de variância (ANOVA, p<0,05). Os resultados dos testes de flexão e fratura foram respectivamente: G0 - 58,406,40; G1 - 83,959,43; G2- 103,4219,17; G3 - 160,7817,30; G4 - 170,4711,28; G5 - 106,3521,96; GI - 303,0262,21 e GII - 402,81131,97. O padrão de fratura foi tratado por Mann-Whitney que observou semelhança estatística entre os grupos. Concluiu-se que o desgaste de pinos de fibra de vidro com pontas diamantadas ou discos de lixa produz alterações micromorfológicas aceitáveis. O corte com alicate deve ser evitado. A customização por desgaste da porção apical de pinos de fibra de vidro diminui a resistência à flexão a valores aceitáveis. Dentes restaurados com pinos de fibra de vidro customizados por desgaste possuem resistência à fratura superior a dentes restaurados com pinos intactos. A customização por desgaste facilita a adaptação do pino ao conduto radicular e preserva a estrutura dental. / The purpose of this study was to evaluate fibre posts (White Post DC/FGM) submitted to customization of the apical portion. Experiment 1: 5 #4 posts were divided into five groups (G) and submitted to different custom adaptation treatments: GA no surface treatment, GB- industrial shaping tool (Dentsply), GC- #3195 fine diamond bur (KG Sorensen), GD- medium-grain paper discs (Sof-Lex/3M/ESPE), GE pliers (Tramontina). The micromorphology of the posts was observed in a scanning electron microscope (ZEISS/DSM 960). Experiment 2: 60 posts of different diameters were divided into six groups: G0 #0.5 posts, G1 #1 posts, G2 #2 posts, G3 - #3 posts; G4 - #4 posts and G5 #4 posts submitted to custom adaptation of the apical portion with paper discs until the diameter was equivalent to #2 posts. The posts were submitted to a 3 point bending test in a universal testing machine (Instron/5500 R), according to ISO 10477. Experiment 3: 20 freshly extracted permanent healthy human canines with similar size were endodontically treated and the crowns were removed, leaving a remaining root length of 15 mm. The teeth were embedded in acrylic resin with simulation of the periodontal ligament, received a 2 mm ferule and were divided into two groups: G1- 10 #4 posts were cemented into post spaces prepared with #4 drill (FGM) at 10 mm, G2 - 10 #4 customized posts were cemented into root spaces prepared with #2 drill (FGM) at 10 mm and #4 drill (FGM) at 5 mm. The posts were cemented with resin cement (Rely X U100/3M/ESPE), and the teeth received direct crowns of composite resin (Enforce Core/Dentsply), standardized with polycarbonate crowns (TDV). The fracture strength was measured on an Instron, at 45 degrees to the long axis of the tooth, until fracture. The 500 N cylindrical load was applied to the buccal/lingual axis 2 mm below the incisal line, at crosshead speed of 0.5 mm/min. The fracture pattern was observed and classified as favorable or unfavorable. The results were submitted to ANOVA (p<0.05). Flexural strength and resistance to fracture data were, respectively: G0 58.40+6.40; G1 83.95+9.43; G2 103.42+19.17; G3 160.78+17.30; G4- 170.47+11.28; G5 106.35+21.96;GI 303.02+62.21 and GII 402.81+131.97. Fracture patterns were statistically similar according to Mann-Whitney test. It was concluded that customization of fibre posts with diamond burs or paper discs produces acceptable micromorphological changes. The cut of the post with pliers should be avoided. Grounding of the apical portion of fibre posts reduces the flexural strength to acceptable values. Teeth restored with grounded fiber posts have grater fracture strength than teeth restored with intact posts. Grounding of the post facilitates adaptation to root walls and preserves tooth structure.
| Identifer | oai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:BDTD_UERJ:oai:www.bdtd.uerj.br:2709 |
| Date | 25 January 2012 |
| Creators | Ana Regina Cervantes Dias |
| Contributors | Mauro Sayão de Miranda, Marcos de Oliveira Barceleiro, Adalberto Bastos de Vasconcellos, Hélio Rodrigues Sampaio Filho, Márcio Antônio Paraizo Borges, Teresa Cristina Ávila Berlinck |
| Publisher | Universidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Odontologia, UERJ, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0034 seconds