Resistivity measurements in thin film samples depending on the temperature and on the
film thickness is always a subject of interest, above all when it comes to new materials.
This work presents the implementation of a measuring system for thin film resistivity
based on four probes showing the dependency of the resistivity on the temperature as
well as on the film thickness. In order to change the temperature of the samples, a heat
source based on a Peltier element was implemented into the measuring system. A
Graphical User Interface using a LabVIEW software controls all the devices of the
measuring system and allows the user to calculate the thin film resistivity choosing
between four measuring method: Van der Pauw, Modified Van der Pauw, Linear Van der
Pauw and Linear Four Probes methods.
Resistivity in aluminum and tungsten thin film samples with 100, 300, and 600 nm
thickness were measured at temperatures between 303K and 373K with increments of
5 K. The results obtained are higher than bulk resistivity values and agrees with the
present theory. Moreover, it is shown that the resistivity values obtained and its
corresponding temperature coefficients increases as the film thickness decreases. / Tesis
| Identifer | oai:union.ndltd.org:PUCP/oai:tesis.pucp.edu.pe:123456789/8900 |
| Date | 28 June 2017 |
| Creators | Salas Casapino, Carlos Alberto |
| Contributors | Guerra Torres, Jorge Andrés, Ströhla, Tom |
| Publisher | Pontificia Universidad Católica del Perú |
| Source Sets | Pontificia Universidad Católica del Perú |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Source | Pontificia Universidad Católica del Perú, Repositorio de Tesis - PUCP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds