Previous issue date: 2012-03 / Este trabalho apresenta uma avaliação acustoelástica em seis tubos OCTG API 5CT Grau N80Q do tipo Casing, soldados pelo processo ERW/HFIW, utilizados na prospecção e exploração de petróleo e gás. A técnica ultrassônica da birrefringência acústica foi usada para avaliar o comportamento acustoelástico da chapa de aço que deu origem aos tubos em estudo. Antes e após as etapas de tratamento térmico de têmpera/revenido e de desempeno a quente os tubos também foram avaliados acustoelasticamente. A constante acustoelástica do material foi obtida por ensaio de carregamento uniaxial em oito cargas pré-determinadas. A avaliação acustoelástica dos tubos mostra uma anisotropia acústica de nível reduzido quando comparados a tubos API 5L com solda. Foi verificada ainda uma redução do nível de anisotropia após cada uma das etapas de fabricação avaliadas, mostrando a eficácia do tratamento térmico de têmpera/revenido e do desempeno a quente. Foi determinada a tensão residual circunferencial existente em um tubo pela técnica ultrassônica da birrefringência acústica e comparada com a tensão obtida pela metodologia da norma ASTM E1928-07. / This paper presents an acoustoelastic evaluation of six OCTG API 5CT N80Q casing pipes welded by ERW/HFIW process, which are used in oil and gas exploration and exploitation. The ultrasonic technique of acoustic birefringence was employed to evaluate the acoustoelastic behavior of the steel plate used to manufacture the pipes under study. The pipes were evaluated before and after the heat treatments of quench tempering and hot straightening were performed. The acoustoelastic constant of the material was obtained through an uniaxial loading test at eight predetermined loads. The results obtained for the pipes show a reduced level of acoustic anisotropy compared with the API 5L welded pipe. A reduction in the level of acoustic anisotropy was also verified after each manufacturing step, showing the efficacy of the heat treatment of quench tempering and hot straightening. The circumferential residual stress in a pipe was determined by the acoustic birefringence technique and compared with the value obtained by the methodology of the ASTM E1928-07 Standard.
| Identifer | oai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/1902 |
| Date | 03 1900 |
| Creators | Fonseca, Manoel Antonio da Costa, Instituto de Engenharia Nuclear |
| Contributors | Payão Filho, João da Cruz, Pereira, Gabriela Ribeiro, Bittencourt, Marcelo de Siqueira Queiroz, Pereira, Cláudio Márcio do Nascimento Abreu, Payão Filho, João da Cruz |
| Publisher | Instituto de Engenharia Nuclear, Programa de Pós-Graduação em Engenharia em Ciências Metalúrgicas e de Materiais, IEN, Brasil, Universidade Federal do Rio de Janeiro |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds