Diploma thesis is focused on comparison of small punch test results and tensile test results. For experiments were chosen steel P91, 10Ch2MFA, 20CrNi2MoV, 11 416 and 42 2707. These steel are used in nuclear power engineering, or they were developed for this purpose. Basic mechanical characteristics, namely ultimate tensile stress and yield stress, were evaluated from small punch test records of observed materials. This is done via convenient correlation relationships. Obtained values were compared with values obtained by conventional tensile tests. There are mentioned own suggested correlation relationships and comparison of temperature curves gained from small punch test and tensile test in the thesis. Assessment of microstructure of observed materials and analysis of fracture surfaces was provided as well. It was found out, that for assessing basic mechanical characteristics (ultimate tensile stress and yield stress) is the best to suggest own correlation relationships, instead of using universal relationships from literature. The fracture mechanism of all types of assessed steel was ductile in entire temperature range (up to -40 °C).
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230953 |
| Date | January 2013 |
| Creators | Němčíková, Eva |
| Contributors | Hůlka, Jiří, Hadraba, Hynek |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds