Glass forming ability (GFA) in the Pr-rich Pr-(Cu, Ni)-Al alloys at or near the eutectic points was systematically studied. It was found that the GFA in the pseudo-ternary alloys of Pr-(Cu, Ni)-Al is higher than that of the ternary alloys of Pr-Cu-Al. Two eutectic compositions in Pr-(Cu, Ni)-Al alloys were found by DSC, namely, Pr₆₈(Cu₀.₅Ni₀.₅)₂₅Al₇ and Pr₅₂(Cu₀.₅Ni₀.₅)₂₅Al₂₃ (at %). The later one shows better GFA than the first one. However, the best GFA was obtained at an off-eutectic composition of Pr₅₄(Cu₀.₅Ni₀.₅)₃₀Al₁₆, which can be formed in fully amorphous rod with diameter of 1.5 mm by copper mould casting. The deviation of the best GFA composition from the eutectic point [Pr₆₈(Cu₀.₅Ni₀.₅)₂₅Al₇] was explained in terms of the asymmetric coupled eutectic zone and the higher glass transition temperature Tg on the hypereutectic side. / Singapore-MIT Alliance (SMA)
| Identifer | oai:union.ndltd.org:MIT/oai:dspace.mit.edu:1721.1/3974 |
| Date | 01 1900 |
| Creators | Zhang, Yong, Li, Yi |
| Source Sets | M.I.T. Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Article |
| Format | 609888 bytes, application/pdf |
| Relation | Advanced Materials for Micro- and Nano-Systems (AMMNS); |
Page generated in 0.0018 seconds