Dissertação (mestrado)—Universidade de Brasília, Instituto de Química, Programa de Pós-Graduação em Química, 2014. / Submitted by Alaíde Gonçalves dos Santos (alaide@unb.br) on 2014-04-15T11:39:00Z
No. of bitstreams: 1
2014-MatheusSerradeHolanda.pdf: 3586279 bytes, checksum: f4230d2a852ae95eaf1670a9d62e4cb8 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2014-04-24T14:52:46Z (GMT) No. of bitstreams: 1
2014-MatheusSerradeHolanda.pdf: 3586279 bytes, checksum: f4230d2a852ae95eaf1670a9d62e4cb8 (MD5) / Made available in DSpace on 2014-04-24T14:52:46Z (GMT). No. of bitstreams: 1
2014-MatheusSerradeHolanda.pdf: 3586279 bytes, checksum: f4230d2a852ae95eaf1670a9d62e4cb8 (MD5) / Fibras de TiO2 dopadas com európio e/ou cério foram produzidas através do método de electrospinning e calcinadas a 500 e a 700 °C. Análises de MEV mostraram que fibras com diâmetro médio de 294 nm foram obtidas e analises de MET mostram que, ao serem dopadas, as fibras são formadas por cristalitos de menor tamanho. Analises EDS mostram que a distribuição do dopante na fibra foi homogênea. Os difratogramas apresentam a presença de diferentes fases cristalográficas e mostram que a temperatura de 500 °C é ideal para a formação da fase anatase, ativa para fotocatálise, e que, para a formação dessa fase, é ideal uma baixa porcentagem do dopante e um dopante de menor raio iônico. As fibras dopadas com európio apresentam picos de excitação e de emissão característicos. Os testes de fotocatálise revelaram que as fibras dopadas apresentam um maior poder de degradação dos poluentes orgânicos. _______________________________________________________________________________________ ABSTRACT / TiO2 fibers doped with europium and/or cerium were produced by electrospinning method and calcined at 500 °C and 700 °C. SEM analysis showed that fibers with average diameter of 294 nm were obtained and TEM analysis showed that, by being doped, the fibers are formed by smaller crystallites. EDS analysis pointed out that a homogeneous distribution of the dopant on the fibers was achieved. The difratogramas presented different crystallographic phases and showed that the temperature of 500 ° C is ideal for the formation of anatase phase, active for photocatalysis, and that, for the formation of this phase is ideal a low percentage of doping and a smaller ionic radius doping. Europium doped fibers present excitation and emission characteristic signals. Photocatalysis tests revealed that the doped fibers have greater power of degradation of inorganic pollutants.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/15490 |
| Date | January 2014 |
| Creators | Holanda, Matheus Serra de |
| Contributors | Rodrigues, Marcelo Oliveira |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds