Thesis (M. Sc. (Physics)) -- University of Limpopo, 2021 / Titanium is the most abundant element in the earthβs crust and can be produced as both
a metal and in powder form. It finds applications in various industries such as in medical
and aerospace, where the fabrication of components with excellent corrosion and high temperature performance are significant. This metal also plays a significant role in the
titanium production process due to its desirable physical and chemical properties.
However, this process occurs in the presence of alkali metal and alkali earth metal salt
mediums. In this study, a combination of computational modelling techniques was
employed to investigate the LiCl, TiCl, TiCl2 and TiCl4 systems and their interaction with
titanium cluster (Ti7) at various temperatures. The density functional theory-based codes
were used to study the structures and stability, while the classical force-fields codes were
employed to study the temperature effect on these systems.
Firstly, the LiCl model was validated using Buckingham interatomic potentials from the
Catlow-library, employing the GULP code. The selected potential parameters were able
to reproduce the LiCl structure to within 1% in agreement with experimental data.
Furthermore, the Ti-Cl and Ti-Li interatomic potential parameters from accurate first principle calculations describe the interaction of LiCl and Ti7 cluster. The new interatomic
potential parameters were deduced as Ti-Cl: π·π= 0.400, π0= 1.279, π0=2.680 and Ti-Li:
π·π =0.730, π0=1.717, π0=2.000.
vi
Secondly, DL_POLY code was used to characterise both the bulk LiCl and Ti7/LiCl
structures employing rigid ion and shell models. It was found that the diffusion coefficient
of LiCl was 6.26 nm2
/s, which corresponds to the melting temperature range of 700 K β
800 K for the rigid ion model. This agrees well with the experimental melting temperature
range of 877 K β 887 K. The shell model predicts a lower melting temperature range of
600 K β 700 K at a diffusion coefficient of 3.74 nm2
/s, compared to rigid ion model. This
behaviour was confirmed by the broadness of peaks on the RDF graphs at this
temperature. The RDF graphs for the Ti7/LiCl structure in both rigid ion model and shell
model depict a change in the morphology of the system for all interactions as the
temperature is increased. It was found that the shell model is preferential for the LiCl
structure.
Thirdly, the elastic and mechanical properties of the TiCl, TiCl2 and TiCl4 structures were
evaluated. It was found that the TiCl2 and TiCl4 structures are elastically unstable.
However, the mechanical properties indicated that TiCl2 and TiCl4 are mechanically
stable. The TiCln structures, namely TiCl and TiCl2, were evaluated for rigid ion model, to
check the transferability of potentials. It was found that the diffusion coefficient of TiCl was
32.02 nm2
/s, which corresponds to a melting temperature of 700 K. The diffusion
coefficient for TiCl2 was 115.00 nm2
/s at a melting temperature of 800 K.
Lastly, molecular dynamics calculations carried out on the Ti7/TiCln structure showed that
an increase in temperature results in the broadening of peaks and a decrease in the peak
heights. The entropy and Gibbs formation free energy for LiCl (rigid ion and shell models),
vii
TiCl and TiCl2 (rigid ion model) structures were estimated to determine the influence of
temperature on the structures. It was found that the LiCl (shell model) structure is stable
at all temperatures and that the TiCl and TiCl2 structures are favoured at lower
temperatures (< 500 K). These results provided new insight into understanding the
reactions and interactions of titanium clusters with salt mediums in titanium production
processes. Moreover, the findings may contribute towards developing alternative ways of
titanium production in continuous and less expensive processes. / Royal Society Advanced Fellowship Newton Grant
(NA140447); National Research Foundation (NRF) and
Titanium Centre of Competence (TiCoC)
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:ul/oai:ulspace.ul.ac.za:10386/3763 |
| Date | January 2021 |
| Creators | Mazibuko, Andile Faith |
| Contributors | Chauke, H. R., Ngoepe, P. E. |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | xviii, 173 leaves |
| Relation |
Page generated in 0.0027 seconds