The focus of the project was to alter and optimize the water repellant textile coating formulations to reach enhanced durability. For this purpose, the project was approached with three methods. Firstly, bio-based components were implemented in the mother emulsion to act as surfactant and crosslinking agent and to provide hydrophobic properties. Secondly different binders were added to crosslink and increase the coating resistance towards washes. Lastly additives at nano-scale were added to increase surface roughness in order to obtain higher hydrophobicity and improved of crosslinking capacity due to the presence of more functional groups. The stability of all emulsions was controlled using different techniques such as optical microscopy to determine particle size, distribution and any observable instability (flocculation etc.), normal aging at room temperature and accelerated aging using higher temperature. All coatings were applied using a laboratory padder on standard PA and PES pieces of textiles and hydrophobic performance was evaluated through ISO 4920 spray test. By standard washing and repeating spray test, durability could be assessed. Further structure and property studies have been run using other tests such as: contact angle measurement, breathability of the coating and SEM observations. Based on the obtained results the incorporation of low HLB, bio-based surfactants in low amount (~0,25%) resulted in an increase in the hydrophobic performance of the tested textiles. However, a decrease in shelf life could be observed with these surfactants at room temperature. Sonication was successfully used to increase both stability and shelf life significantly. Some binders and nanoparticles proved to be successful in increasing the coating quality and thus the durability. Overall many of the developed formulations could enhance performance on PA compared to the already present commercial product. On PES textile, however, the developed strategies yielded hydrophobic effect close to the commercial product.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-213517 |
Date | January 2017 |
Creators | Solomon, Meron |
Publisher | KTH, Skolan för kemivetenskap (CHE) |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds