Previous issue date: 2013-04-25 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260?C. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface / O objetivo desse trabalho foi a obten??o de nanopart?culas de ?xido de ferro, a magnetita (Fe3O4), via s?ntese por decomposi??o t?rmica via poliol, avaliando assim duas rotas: a rota simples decomposi??o assistida por refluxo e a rota hidrot?rmica, ambas sem atmosfera de ar sint?tico e usando a temperatura de s?ntese de 260?C. Observou-se nesse trabalho a influ?ncia da aus?ncia de surfactantes, comumente utilizados em s?nteses de ?xidos de ferro, com a finalidade de promover uma melhor dispers?o das nanopart?culas, diminuindo assim as ?reas de aglomerados. Al?m disso, visou-se: a obten??o de uma fase puramente de magnetita, sem a forma??o de fases secund?rias comumente encontradas nas s?nteses dos ?xidos de ferro; um melhor controle do tamanho de cristalito; da morfologia; da estrutura cristalina e do comportamento magn?tico. Por fim, analisou-se a introdu??o dos grupos hidroxilas na superf?cie das nanopart?culas, e sua empregabilidade na produ??o de pol?meros com radicais (OH). Os materiais obtidos foram caracterizados por an?lises de DRX, DLS, VSM, TEM, TG e DSC. Os resultados foram satisfat?rios quanto ? obten??o da magnetita, com tamanho de part?cula maior que 5 nm e menor que 11 nm, de morfologia bem definida e com boas propriedades magn?ticas com comportamento superparamagn?tico. Quanto ? deposi??o dos grupos de hidroxilas na superf?cie das nanopart?culas, a s?ntese com refluxo mostrou-se mais eficiente
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12820 |
| Date | 25 April 2013 |
| Creators | Costa, Tharsia Cristiany de Carvalho |
| Contributors | CPF:06296687877, http://lattes.cnpq.br/2365059843175411, Motta, Fabiana Villela da, CPF:24779953839, http://lattes.cnpq.br/9918299069511517, Santos, I?da Maria Garcia dos, CPF:50548220115, http://lattes.cnpq.br/7060067415685353, Melo, Jos? Daniel Diniz, CPF:46660640444, http://lattes.cnpq.br/6572298923055649, Delmonte, Mauricio Roberto Bomio, CPF:27816279841, http://lattes.cnpq.br/9558299312183852, Silva, M?rcia Rejane Santos da, CPF:00986664448, http://lattes.cnpq.br/7632449835328149, Paskocimas, Carlos Alberto |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds