In this thesis, multiple activities have been carried out in order to improve the process of CIGSS solar cell fabrication on a 4" x 4" substrate. The process of CIGSS solar cell fabrication at FSEC's PV Materials Lab involves a series of steps that were all carried out manually in the past. A LABVIEW program has been written to carry out automated sputter deposition of Mo back contact, CuGa, In metallic precursors on a soda lime glass substrate using a stepper motor control for better uniformity. Further, selenization/ sulfurization of these precursors was carried out using rapid thermal processing (RTP). CIGS films were sulfurized using chemical bath deposition (CBD). ZnO:Al was deposited on the CIGSS films using RF sputtering. A separate LABVIEW program was written to automate the process of ZnO:Al deposition. Ni/Al contact fingers were deposited on the ZnO:Al layer using the e-beam evaporation technique. Further, in order to test these solar cells in-house, a simple current-voltage (IV) tracer was fabricated using LABVIEW. A quantum efficiency (QE) measurement setup was built with guidance from the National Renewable Energy Laboratory (NREL). Lastly, analysis of data from photovoltaic (PV) modules installed on the FSEC test site has been carried out using a LABVIEW program in order to find out their rate of degradation as time progresses. A 'C' program has also been written as an aid for keeping a daily log of errors in data and for troubleshooting of the same.
| Identifer | oai:union.ndltd.org:ucf.edu/oai:stars.library.ucf.edu:etd-1618 |
| Date | 01 January 2005 |
| Creators | Shirolikar, Jyoti |
| Publisher | STARS |
| Source Sets | University of Central Florida |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Electronic Theses and Dissertations |
Page generated in 0.0022 seconds