Organic semiconductors are envisioned to have widespread applications in flexible displays, radio-frequency identification (RFID) tags, bio- and chem-sensors, as well as organic solar cells. Polymer semiconductors are particularly suitable for the low-cost manufacture of organic electronics using printing techniques due to their excellent solution processability and mechanical properties. This work focuses on the development of two novel building blocks, IBDF and DTA, which can be used for the construction of high performance organic thin film transistors (OTFTs) and organic photovoltaics (OPVs). Two copolymers, P6-IBDF-T and P5-IBDF-T, and a homopolymer P6-IBDF were prepared using the IBDF building block. Copolymer P6-IBDF-T has been prepared via the Stille-coupling polymerization. This polymer exhibits a small band gap of 1.36 eV with HOMO/LUMO energy level of -5.69 eV/-4.43 eV. P6-IBDF-T showed stable electron transport performance in encapsulated thin film transistors and ambipolar transport performance in non-encapsulated TFTs. Balanced hole/electron mobilities of up to 8.2 ??10-3/1.0 ??10-2 cm2V-1s-1 was achieved in bottom-contact, bottom-gate organic thin film transistors. In addition, the broad absorption of the polymer over the UV-Vis range suggested that this polymer is suitable for applications in solar cells. The effect of conjugation on mobility and UV-vis spectra of the polymer was studied by comparing P5-IBDF-T with P6-IBDF-T. The ideal of indirect electron transition was proposed to explain the difference between UV-Vis light absorption spectra for these two polymers.
DTA building block was used to construct four D-A copolymers, namely PDTA-T, PDTA-BT, PDAT-BTV, and PDTA-TT. These polymers were characterized by UV-Vis, CV, DSC, TGA, AFM and XRD. Device performance was also investigated on OTFTs. The device performance of DTA based polymer increased as the area of electron donor increase from T in PDTA-T to BTV in PDTA-BTV. PDTA-BTV exhibits hole mobility of 1.3??10-3 cm2 V-1 s-1 with Ion/Ioff value of ~103-4 in bottom-contact, bottom-gate organic thin film transistors. All DTA based copolymers exhibited small optical bandgaps (1.18 ??? 1.27 eV) and required none or moderate thermal treatment during fabrication process. These make them promising candidates for cost-effective OPV applications.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OWTU.10012/7771 |
| Date | 06 November 2014 |
| Creators | Yan, Zhuangqing |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
Page generated in 0.0016 seconds