Orientador: Regina Maria Puppin-Rontani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T15:49:42Z (GMT). No. of bitstreams: 1
Araujo_GiovanaSpagnoloAlbamontede_D.pdf: 1143246 bytes, checksum: 8603c02b2d586d6acf3433f2f35cda3b (MD5)
Previous issue date: 2015 / Resumo: Os objetivos desta tese composta por dois capítulos foram: Capítulo 1- Avaliar a estabilidade de cor e efetividade de tratamentos clareadores em lesões iniciais em esmalte infiltradas com Icon®. Capítulo 2- Avaliar a efetividade do clareamento com um gel experimental contendo natrosol substituindo o carbopol e avaliar a degradação causada no infiltrante por estes géis. Capítulo 1: Foram confeccionados espécimes à partir de dentes bovinos (N=30, 5x5x3mm) e divididos em três grupos (n=10): controle, desmineralizado e infiltrado. Lesões subsuperficiais artificiais foram desenvolvidas utilizando solução para produção de cárie, exceto no grupo controle (esmalte hígido). Nos espécimes do grupo infiltrado, após o desenvolvimento das lesões foi aplicado Icon®(DMG, Hamburgo, Alemanha). Medidas iniciais de cor foram realizadas utilizando espectrofotômetro (CM-700d, Konica Minolta), utilizando o sistema CIE L*a*b*. Os espécimes foram imersos em café, três vezes ao dia, durante 15 minutos, por 14 dias e em seguida armazenados em saliva artificial. Após a pigmentação, medidas de cor foram realizadas novamente. Os espécimes foram submetidos ao clareamento com gel de peróxido de carbamida 16%, por 4h diárias durante 21 dias, e medidas finais de cor foram realizadas. Para comparar medidas iniciais e finais, foi aplicado o teste-t (?=0,05). A comparação entre os grupos foi realizada por ANOVA 1 fator e teste de Tukey (?=0,05). A pigmentação com café promoveu redução significativa nos valores de L* e aumento nos valores de a* e b* em todos os grupos (controle, clareado e infiltrado). O clareamento promoveu aumento nos valores de L* e redução nos valores de a* and b* em todos os grupos. Não houve diferença nos valores de ?E entre os grupos cariados e infiltrados antes do clareamento. Após o clareamento, o grupo infiltrado apresentou os menores valores de ?E, similares ao controle. Pode-se concluir que o esmalte infiltrado com Icon® apresentou alteração de cor após a pigmentação, similares ao esmalte cariado. Entretanto, se ocorrer pigmentação em dentes infiltrados, o tratamento com géis clareadores pode ser realizado com sucesso. Capítulo 2: Foram confeccionados 50 espécimes de infiltrante (Icon®, DMG, Hamburgo, Alemanha), divididos em 5 grupos (n=10), de acordo com o gel a ser exposto: controle (G1), peróxido de carbamida 16% com natrosol (G2), peróxido de carbamida 16% com carbopol(G3), natrosol(G4), carbopol(G5). Os tratamentos foram realizados durante 21 dias, 4 horas ao dia. Medidas de dureza Knoop (HMV-2, Shimadzu), rugosidade (Surfcorder SE1700, Kosaka), análise de cor utilizando espectrofotômetro (CM-700d, Konica Minolta) e imagens de microscopia por força atômica (EasyScan 2, Nanosurf) foram realizadas. Além disso, 50 blocos obtidos à partir de dentes bovinos foram submetidos à pigmentação com chá preto e clareamento utilizando os géis citados acima. Os resultados foram submetidos a ANOVA 1-fator para comparação entre os grupos e teste-t para comparação inicial e final de cada grupo (?=0,05). Pode ser observada redução de dureza nas amostras de Icon® após aplicação do peróxido de carbamida, independente do espessante (G2 inicial: 13,21/final:10,99 e G3 inicial:12,00/final:11,33). Comparando-se todos os grupos após o tratamento, o G4 apresentou maior valor de dureza (13,92), seguido pelo G1(12,77) e G5(12,27). Houve aumento de rugosidade após o tratamento em todos os grupos, porém não houve diferença estatística entre os grupos. Através das imagens de microscopia por força atômica pode-se observar maior irregularidades na superfície do G5. Em relação à efetividade do clareamento, os grupos G2 e G3 promoveram aumento nos valores de L* e maiores valores de ?E. Os grupos G4 e G5 apresentaram valores de L* semelhantes. Pode-se concluir que o peróxido de carbamida associado com natrosol ou carbopol é eficaz no clareamento de dentes infiltrados com Icon®, porém causam degradação superficial no infiltrante / Abstract: The objectives of this thesis, accomplished on two chapters, were: Chapter 1- To evaluate color stability of white spot lesions with Icon® after staining and the bleaching effect in the infiltrated and stained surfaces. Chapter 2- to evaluate surface degradation of Icon® after application of bleaching gels containing natrosol as a thickener and their bleaching effectiveness. Chapter 1- Enamel-dentine specimens (N=30, 5x5x3mm, 1 mm enamel + 2 mm dentine thickness) were prepared from bovine incisors and randomly allocated into three groups (n=10): control, demineralized, infiltrated. Artificial enamel subsurface lesions were created using 50 mL of 0.05 M acetate buffer solution. Specimens were produced by the Icon®(DMG, Hamburgo, Alemanha) application in the enamel caries like-lesions. Baseline color reading were assessed using a spectrophotometer (CM-700d, Konica Minolta), and CIE L*a*b* measurements of each specimen were performed using a white background. In order to simulate extrinsic dietary staining, specimens were placed into 4 mL coffee infusion, three-times daily for 15 minutes, for 14 days. After the staining procedure, color measurements were performed again. Then, bleaching procedures were performed using 16% carbamide peroxide gel, for 4h daily, for 21 days and final measure assessment was performed. To compare baseline and final measurements, t-test was used (p<0.05). The statistical comparison between groups was performed using one-way ANOVA and Tukey tests (p<0.05). Coffee staining provided a significant reduction of L* values and increase of a* and b* in all groups (control, decayed and infiltrated). Bleaching procedure provided a significant increase on L* and decrease of a* and b* values in all groups. There was no significant difference on ?E values between decayed and Infiltrated groups before bleaching, and after bleaching, infiltrated group showed the lowest ?E values. It can be concluded that enamel infiltrated with Icon present significant color alteration after staining, when compared to sound enamel. However, if the infiltrant discoloration occurs, bleaching treatment can be used successfully. Chapter 2 - 50 specimens of infiltrant (Icon®, DMG, Hamburgo, Alemanha) were produced and allocated into 5 groups (n = 10) in accordance with the gel were made to be exposed: Control (G1), carbamide peroxide 16% with natrosol (G2), carbamide peroxide with carbopol (G3), natrosol (G4), carbopol (G5). Bleaching treatments were performed for 21 days, 4 hours per day. Hardness Knoop measurements (HMV-2, Shimadzu), roughness measurements (Surfcorder SE1700, Kosaka), and atomic force microscopy images (EasyScan 2, Nanosurf) were performed after bleaching treatments. In addition, the 50 blocks obtained from bovine teeth were submitted to bleaching treatment with gels mentioned above. The results were subjected to ANOVA one-way for comparison between groups and t-test for comparing initial and final of each group (?<0.05). Knoop Hardness decreased can be observed after application of carbamide peroxide, regardless of thickener (initial G2: 13.21 / final: 10.99 and G3 initial: 12.00 / final: 11,33). Comparing all groups after treatment, G4 showed higher hardness Knoop value (13.92), followed by G1 (12.77) and G5 (12.27). After bleaching, there was roughness increase for all groups, and there was no statistical difference between them. Atomic force microscopy images show higher surface irregularity in G5. Regarding bleaching effectiveness, G2 and G3 groups presented increase in L * values and highest ?E values. G4 and G5 groups showed statistically similar L* values. It can be concluded that carbamide peroxide with natrosol and carbamide peroxide with carbopol may cause surface degradation. Carbamide peroxide associated with natrosol or carbopol is effective in whitening teeth infiltrated with Icon®. Further studies should be performed to evaluate the leaching of components infiltrating subjected to degradation over time / Doutorado / Materiais Dentarios / Doutora em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288600 |
| Date | 24 February 2015 |
| Creators | Araújo, Giovana Spagnolo Albamonte de, 1986- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Puppin-Rontani, Regina Maria, 1959-, Boscarioli, Ana Paula Teixeira, Hofling, Roberta Tarkany Basting, Paula, Andreia Bolzan de |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 43 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds