O objetivo deste estudo foi avaliar a resistência de união (RU) do esmalte e da dentina decídua após desafio erosivo utilizando sistemas adesivos convencionais e autocondicionantes. Noventa e seis molares decíduos foram seccionados mesio-distalmente para obtenção de blocos de esmalte, foram embebidos em resina epóxi e polidos com lixas de carbeto de silício (600, 1200, 2400 e 4000). As amostras foram randomizadas e divididas entre os 4 sistemas adesivos utilizados: SB (Adper Single Bond 2), SBU (Single Bond Universal), OBFL (Optibond FL) e BF (Bond Force). Metade das amostras (grupo teste, n=48) foram submetidas a desafio erosivo/abrasivo (50 mL de Coca-Cola®, pH 2,6, 1 min, 4x ao dia, 5 dias, seguido de escovação por 1 min com dentifrício fluoretado, NaF 1450 ppm e saliva artificial). A outra metade dos blocos (grupo controle) foi mantida imersa em saliva artificial. Em seguida foram realizadas restaurações de resina flow (Tetric Flow) utilizando matrizes de polivinil siloxano com diâmetro de 0,9mm e 1mm de altura. As amostras foram colocadas na máquina de ensaio universal e foi aplicada força de cisalhamento com velocidade de 1,0mm/min até que a fratura ocorresse. Os mesmos blocos tiveram suas superfícies de dentina expostas, em seguida, as mesmas etapas foram realizadas (restaurações e RU). Foram utilizados os testes ANOVA de duas vias e Tukey (p=0,05). No esmalte, os grupos teste e controle não apresentaram diferença estatística, independentemente dos sistemas adesivos utilizados. Na dentina, o BF apresentou melhores valores de no grupo teste (p=0,04). O fator adesivo foi significativo na análise fatorial (p<0,001) assim como a interação entre desafio erosivo/abrasivo e os sistema adesivo utilizado (p=0,046). Somente o substrato dentinário teve influência significativa na RU (p=0,395). Conclui-se que a RU ao esmalte decíduo não foi afetada pelo desafio erosivo/abrasivo para todos os sistemas adesivos utilizados, enquanto a RU na dentina decídua somente foi afetada pelo sistema adesivo autocondicionante contendo flúor. / The aim of this in vitro study was to evaluate the microshear bond strength of four adhesive systems on eroded or sound primary teeth. Methods: Ninety-six primary molars were cut mesio-distally, embedded, ground and polished with SiC papers (600, 1200, 2400 and 4000). Specimens were randomly divided according to 4 adhesive systems: SB (Adper Single Bond2®), SBU (Universal Single Bond®), OBFL (OptibondFL®) and BF (BondForce®). Half of the specimens were exposed to erosive/abrasive challenge, and the other half (control group; n=48) remained immersed in artificial saliva. Erosive challenge consisted of specimen immersion in Coca-Cola® (pH 2.6, 50ml, 1min, 4x, 5 days). Once a day, the specimens were brushed using an electric toothbrush with a slurry (artificial saliva and NaF toothpaste, 1450 ppm) for 1 minute. Polyvinyl siloxane molds with a perforation 0.9 mm in diameter and 1 mm in height were placed over the specimens in order to build restorations with flowable resin composite. The molds were cut with surgical blades and removed to allow for microshear bond strength testing. Bonded specimens were attached to an universal testing machine and a shear load was applied with a steel wire at a crosshead speed of 1.0 mm/min until failure occurred. After the tests in enamel, dentin was exposed and polished to perform the same tests in this substrate. Two-way ANOVA and Tukey tests were performed (p=0.05). Results: No statistically significant difference was found between the eroded and sound enamel for any of the adhesives. BF was statistically significant better in eroded dentin than sound dentin (p=0.04). A factorial analysis indicated that the factor adhesive was significant (p<0.001) as was the interaction between adhesive and erosive tooth wear (p=0.046). Only the dentin substrate had a significant influence on microshear bond strength (p=0.395). Conclusion: Bond strength to primary enamel was not affected by erosive/abrasive challenge for all the adhesives systems, while in primary dentin the bond strength was affected only after the use of self-etch adhesive containing fluoride.
| Identifer | oai:union.ndltd.org:IBICT/oai:lume56.ufrgs.br:10183/152683 |
| Date | January 2016 |
| Creators | Santos, Nicole Marchioro dos |
| Contributors | Rodrigues, Jonas de Almeida |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFRGS, instname:Universidade Federal do Rio Grande do Sul, instacron:UFRGS |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds