Avaliação de um sistema híbrido de tratamento de águas: membrana cerâmica de microfiltração com resina trocadora iônica. / Evaluation of a hybrid water treatment system: ceramic microfiltration membrane with ion exchange resin.

Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-03-23T20:01:22Z
No. of bitstreams: 1
JULYANNA DAMASCENO PESSOA - DISSERTAÇÃO PPGEQ 2015..pdf: 3056060 bytes, checksum: f1c90789fd3af9574cb10fbc1d69a075 (MD5) / Made available in DSpace on 2018-03-23T20:01:22Z (GMT). No. of bitstreams: 1
JULYANNA DAMASCENO PESSOA - DISSERTAÇÃO PPGEQ 2015..pdf: 3056060 bytes, checksum: f1c90789fd3af9574cb10fbc1d69a075 (MD5)
Previous issue date: 2014-12-15 / Em decorrência da degradação dos recursos hídricos e da crescente preocupação
com microrganismos específicos na água, a utilização de membranas cerâmicas
para separação de materiais contaminantes, passa a ser uma opção de tratamento
para a produção de água potável, devido a motivos como, por exemplo, sua
resistência ao ataque de produtos químicos, requerer uma menor área de
construção do equipamento, maior economia de energia, dentre outros. O presente
trabalho objetivou estudar o desempenho de um sistema híbrido, composto por
membrana cerâmica tubular de microfiltração, recheadas por resinas trocadoras
iônicas, para tratamento de água de qualidade inferior. As membranas utilizadas
nesse trabalho são do tipo α-alumina (α-Al2O3), tamanho nominal de poro de
aproximadamente 0,8 µm, produzidas pelo Laboratório de Membranas Cerâmicas
(LABCEM) do Laboratório de Referência em Dessalinização (LABDES) na
Universidade Federal de Campina Grande (UFCG). O sistema foi avaliado em
função do fluxo e vazão do permeado, nas pressões de operação 0,5; 1,0; 2,0 e 3,0
bar; teste de presença / ausência e contagem bacteriológicas na água da
alimentação e permeado para o sistema: membrana cerâmica; análises físicoquímicas
realizadas para o sistema: membrana cerâmica/ RTI; e tempo de
residência hidráulica ( ), nas pressões de operação 1,0; 2,0 e 3,0 bar. A membrana
cerâmica removeu completamente os Coliformes totais e fecais (Escherichia coli) da
água. O comportamento do fluxo do permeado variou com a pressão de operação.
No sistema híbrido: membrana cerâmica/ RTI, o tempo de residência foi de 15,55
segundos na pressão de operação 1,0 bar, removendo 71,9% dos íons da água de
alimentação, para 66% na pressão 2,0 bar ( =11,73 segundos) e 61% na de 3,0 bar
( = 10,11 segundos). O sistema híbrido mostrou-se eficiente na remoção dos
parâmetros físico-químicos e produziu água tratada de boa qualidade quanto aos
parâmetros bacteriológicos nas águas de qualidade inferior, com baixo consumo
energético. / Due to the degradation of water resources and the increasing concern about specific
microorganisms in water, the use of ceramic membranes for separation of
contaminating materials, becomes a treatment option for the production of drinking
water, due to reasons such as its resistance to chemicals, requires a smaller area of
equipment construction, greater energy savings, among others. This study
investigated the performance of a hybrid system consisting of a tubular microfiltration
ceramic membrane, filled with ion exchange resins for substandard water treatment.
The membranes used in this work are the α-alumina type (α-Al2O3), with pores
which have a nominal diameter of about 0.8 microns produced by Laboratório de
Membranas Cerâmicas (LABCEM), at Desalination in Reference Laboratory
(LABDES) at the Federal University of Campina Grande (UFCG). The system was
evaluated by the flow and permeate flow, the operating pressure 0.5; 1.0; 2.0 and 3.0
bar; presence / absence and bacteriological count tests in the feed and permeate
water for the system: ceramic membrane; Physical and chemical analysis for the
system: ceramic membrane / RTI; and hydraulic residence time (τ), at the operating
pressures of 1.0; 2.0 and 3.0 bar. The ceramic membrane completely removed the
Total and fecal (Escherichia coli) Coliform of the water. The permeate flux behavior
varied with the operating pressure. In the hybrid system: ceramic membrane / RTI
residence time was 15.55 seconds at the operating pressure of 1.0 bar by removing
71.9% of the feed water ions, to 66% at 2.0 bar pressure ( = 11.73 seconds), and
61% for the 3.0 bar ( = 10.11 seconds). The hybrid system was efficient in the
removal of physical and chemical parameters and produced good quality treated
water as for the bacteriological parameters in lower quality water with low power
consumption.

Identiferoai:union.ndltd.org:IBICT/oai:localhost:riufcg/318
Date23 March 2018
CreatorsPESSOA, Julyanna Damasceno.
ContributorsFRANÇA, Kepler Borges., OLIVEIRA, Laércio Gomes de., LIRA, Hélio de Lucena.
PublisherUniversidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0023 seconds