Electrochromic thin films can effectively regulate the visible and infrared light passing through a window, demonstrating great potential to save energy and offer a comfortable indoor environment in buildings. However, long-term durability is a big issue and the physics behind this is far from clear. This dissertation work concerns two important parts of an electrochromic window: the anodic and cathodic layers. In particular, work focusing on the anodic side develop a new Ni oxide based layers and uncover degradation dynamics in Ni oxide thin films; and work focusing on the cathodic side addresses materials rejuvenation with the aim to eliminate degradation. In the first part of this dissertation work, iridium oxide is found to be compatible with acids, bases and Li+-containing electrolytes, and an anodic layer with very superior long-term durability was developed by incorporating of small amount (7.6 at. %) of Ir into Ni oxide. This film demonstrated sustained cycle-dependent growth of charge density and electrochromic modulation even after 10,000 CV cycles. The (111) and (100) crystal facets in Ni oxide are found to possess different abilities to absorb cation and/or anion, which yields different degrees of coloration and this is very significant for the electrochromic properties. The degradation of charge capacity in Ni oxide has an inevitable rapid decay in the first hundreds of cycles, subsequently combined with a more gradual decay, which is independent of applied potential and film composition. The consistent phenomenon can be very well modeled by power-law or stretched exponential decay; however the two models are indistinguishable in the current stage. Interestingly, in both models, the power-law exponent is 0.2 ≤ p ≤ 0.8, with most of the values around 0.5, in line with normal or anomalous diffusion models. The second part of dissertation work deals with cathodic WO3 and TiO2. WO3 suffers from ion trapping induced degradation of charge capacity and optical modulation upon electrochemical cycling. This speculation is strongly supported by direct evidence from Time-of-Flight Elastic Recoil Detection Analysis (ToF-ERDA). Most importantly, this ion trapping induced degradation can be eliminated by a galvanostatic de-trapping process. Significant ion-trapping takes place when x exceeds ~0.65 in LixWO3. The trapped ions are stable in the host structure, meaning that the ions cannot de-trap without external stimuli. The similar work done on TiO2 significantly complements and extends the work on the recuperation of WO3; the difference is that the trapped ions in host TiO2 seem to be less stable compared with the trapped ions in WO3. Overall, this dissertation presents a refined conceptual framework for developing superior electrochromic windows in energy efficient buildings.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-267111 |
| Date | January 2015 |
| Creators | Wen, Rui-Tao |
| Publisher | Uppsala universitet, Fasta tillståndets fysik, Uppsala |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1651-6214 ; 1323 |
Page generated in 0.0016 seconds