The study focused on analysis of microstructure of sintered TiO2 bulk by using XRD, SEM-EBSD, and TEM. The experiment results showed that sintered samples were rutile phase, besides also found growth twins in sintered sample. The twin plane {101 ̅) was confirmed by SEM-EBSD, TEM-SADP and mathematics transformation matrix. Finally traditional contrast analysis was adopted for determining twin boundary were £\-boundaries and displacement vectors R = 1/n[011].