Orientador : Roseana da Exaltação Trevisan / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-27T22:10:04Z (GMT). No. of bitstreams: 1
Zampolli_DaniellaMachado_M.pdf: 8042922 bytes, checksum: 53f345f393039164e10eb600d4054058 (MD5)
Previous issue date: 2000 / Resumo: Neste trabalho, procurou-se encontrar as melhores junções soldadas, de alumínio e cobre, por ultra-som e por resistência a ponto, através de uma otimização destes processos, com o emprego de um planejamento fatorial completo e do método estatístico da superficie de respo_ Posteriormente, realizou-se uma comparação entre as propriedades especificadas para a peça, resistência ao cisalhamento, resistência ao arrancamento e resistência elétrica. Os materiais utilizados foram as ligas de alumínio AA1100-0e de cobre C1O200, a partir das quais soldou-se as junções alumínio/alumínio, cobre/cobre e alumínio/cobre, utilizadas em um mancal porta-escovas, fabricado pela empresa Robert Bosch do Brasil. Os resultados obtidos mostraram que, de um modo geral, o processo de ultra-som gerou as junções mais apropriadas para aplicação na peça, além de outras vantagens mais específicas complementares, como maior facilidade, rapidez de soldagem e condições de trabalho menos severas ao operador. As junções alumínio/alumínio foram soldadas por ambos os processos, tendo-se obtido resultados bastante próximos. Quanto às junções cobre/cobre e alumínio/cobre, a soldagem mostrou-se válida através do processo de ultra-so_ enquanto que o processo por resistência não foi apropriado para os tipos de materiais utilizados. Para todas as soldagens, as ferramentas estatísticas utilizadas trouxeram resultados confiáveis, já que apresentaram embasamento teórico / Abstract: In this work, the objective was to find the best junctions welded by the ultrasound and the spot resistance welding processes, through an optimization of their main parameters, employing a complete factorial planning and the statistic method of the surface response. Lately, it was performed a comparison among the specified properties for the unions, shear resistance, peel resistance and electric resistance. The utilized materials were the alluminum AAII00-0 and the copper CI0200 alloys, with which the unions alluminumlalluminum, copper/copper and alluminumlcopper were welded, and which are employed in an automotive electric part, produced by the Robert Bosch do Brasil company. The obtained results showed that, in a general way, the ultrasound process produced the most applicable junctions for the part, and also other more specific complementary advantages, like an easier, cleaner and faster welding and some less severe work conditions for the worker. The junctions alluminumlalluminum were welded by both processes, being the results very close one to the other. For the junctions copper/copper and alluminumlcopper, the welding was successful through the ultrasound process, while through the resistance process, the results with the employed materials were not satisfactory. The studied statistical tools brought trustful results for all the experiments, since they were based in theoretical concepts / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265244 |
| Date | 30 October 2000 |
| Creators | Zampolli, Daniella Machado |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Trevisan, Roseana da Exaltação, 1951-, Paredes, Ramon Cortes, Robert, Maria Helena |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 173p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds