Previous issue date: 2010-04-09 / The effect of the addition of bismuth, boron, aluminum, titanium, sulphur and nitrogen in steel 1045 had been investigated to also improve the machinability of the modified steel and its influence in mechanical properties. It is considered to substitute the use of the lead as a used lement to earn in machinability to keep the mechanical characteristics of 1045 steel. They will be presented results of machinability tests, hardness measurements and microstructural characterizations by optical and scanning electron microscopy. The results of the impact tests had indicated that 1045 steel with addition of boron, titanium, nitrogen and sulphur presented the best tenacity whereas the usinabilidade results had indicated the 1045 steel added with boron, bismuth, nitrogen and sulphur as most favorable. / Foram investigados os efeitos da adição do Bismuto, do Boro, do Alumínio, do Titânio, do Enxofre e do Nitrogênio no aço 1045 para melhorar a usinabilidade do aço e também sua influência em propriedades mecânicas. Propõe-se substituir o uso do Pb por Bi como um elemento usado para melhorar a usinabilidade mantendo-se as características mecânicas do aço 1045. São apresentados resultados obtidos dos ensaios de usinabilidade, dureza e caracterizações microestruturais por microscopia óptica e eletrônica de varredura. Os resultados de impacto realizados indicaram que o aço 1045 com adição de boro, titânio, nitrogênio e enxofre apresentou a melhor tenacidade enquanto que os resultados de usinabilidade indicaram o aço 1045 adicionado com B, Bi, Ni e S como o melhor.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede.mackenzie.br:tede/1385 |
| Date | 09 April 2010 |
| Creators | Silva Junior, Rafael Vieira |
| Contributors | Monteiro, Waldemar Alfredo, Andrade, Arnaldo Homobono Paes de, Carrió, Juan Alfredo Guevara |
| Publisher | Universidade Presbiteriana Mackenzie, Engenharia de Materiais, UPM, BR, Engenharia de Materiais |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações do Mackenzie, instname:Universidade Presbiteriana Mackenzie, instacron:MACKENZIE |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds