The effect of annealing conditions on the microstructure evolution of CVD nickel was investigated systematically in the present study by differential scanning calorimetry, optical microscopy and transmission electron microscopy (TEM), upon both ex-situ and in-situ annealing. TEM observation revealed the as-deposited CVD nickel possessed a bi-modal grain structure, with large columnar grains embedded in nanocrystalline matrix. Ultrafine and nano growth twins were present as well as multiply twinned grains with five-fold symmetry. Microstructure observation upon annealing showed that grain growth did not occur until annealing at 400ºC. Detwinning was observed at 400ºC and higher temperatures. The ultrafine and nano twins tended to transform into dislocation cell structures and this phenomenon was driven by the excess free energy associated with the high density of grown-in twin boundaries. The five-fold twinned grains were found to be thermally stable up to 600ºC. The hardness was observed to decrease with increasing annealing temperature.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/29512 |
| Date | 23 August 2011 |
| Creators | Chichi, Chen |
| Contributors | Wang, Zhirui |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0017 seconds