Orientadores: Luiz Fernando Zagonel, Mônica Alonso Cotta / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Física Gleb Wataghin / Made available in DSpace on 2017-05-11T13:05:53Z (GMT). No. of bitstreams: 1
Silva, Bruno Cesar da_M.pdf: 3758085 bytes, checksum: 042d8ff5a8d495ad70b0f10c888cd418 (MD5)
Previous issue date: 2016 / Made available in DSpace on 2017-06-14T17:38:47Z (GMT). No. of bitstreams: 1
Silva_BrunoCesarda_M.pdf: 3758085 bytes, checksum: 042d8ff5a8d495ad70b0f10c888cd418 (MD5)
Previous issue date: 2016 / Resumo: Neste trabalho, estudamos a dinâmica de crescimento de nanofios de GaP crescidos pelo método VLS (Vapor-Líquido-Sólido) via Epitaxia por Feixe Químico (CBE), usando nanopartículas catalisadoras de ouro. Investigando o efeito da temperatura na dinâmica de crescimento de nanofios de GaP encontramos uma grande variedade de nanofios em cada amostra, caracterizadas por diferentes direções de crescimento e/ou morfologias, apresentando sempre uma população dominante. Com o aumento da temperatura (510°C) observamos uma transição drástica na morfologia da população dominante, de nanofios típicos para uma nova e inesperada morfologia assimétrica. Mostramos ainda que modificando o tamanho da nanopartícula catalisadora de 5nm para 20nm os nanofios assimétricos ainda são favorecidos a alta temperatura. Procurando compreender o mecanismo de formação dos nanofios assimétricos, mostramos que estas estruturas cristalizam-se na fase WZ, com baixa densidade de defeitos, comparadas às outras amostras. Além disso, mostramos que a assimetria destes nanofios não é oriunda de diferenças de polaridade nas facetas laterais ou formação de defeitos cristalográficos que pudessem modificar a dinâmica de crescimento de modo a levar à morfologia assimétrica. Desta forma, propomos um cenário de crescimento simplificado, no qual a estrutura assimétrica é formada pela combinação do crescimento de nanofios ordinários, via VLS, junto com estruturas que crescem livre de catalizador via mecanismo VS (Vapor-Sólido), estas duas estruturas então se juntam, transferindo material e dando lugar a facetas de menor energia, resultando na formação da estrutura assimétrica. Por fim, medidas de fotoluminescência mostram a emissão característica no verde do GaP WZ para os nanofios assimétricos, mesmo com a estrutura não estando passivada, confirmando a boa qualidade cristalina das nossas amostras / Abstract: In this work, we study the growth dynamics of GaP nanowires grown by VLS (Vapor-Liquid-Solid) method via Chemical Beam Epitaxy (CBE) using gold nanoparticles as catalyst. Investigating the effect of temperature on the growth dynamics of GaP nanowires we find a wide variety of nanowires in each sample, characterized by different growth directions and/or morphologies, always having a dominant population. With increasing temperature (510°C), we observed a dramatic transition in the morphology of the dominant population of typical nanowires to a new and unexpected asymmetric morphology. We also show that modifying the size of the catalyst nanoparticle from 5nm to 20mn the asymmetric nanowires are still favored at high temperature. Looking forward to understand the mechanism of formation of the asymmetric nanowires, we show that these structures crystallize in the WZ phase with low defect density when compared to the other samples. Furthermore, we show that the asymmetry of these nanowires is not derived from differences in polarity in side facets or the formation of crystallographic defects which might modify the growth dynamics so as to bring the asymmetric morphology. Thus, we propose a simplified growth scenario, in which the asymmetric structure is formed by growth combination of ordinary nanowires via VLS, along with structures that grow catalyst-free via VS (vapor-solid) mechanism, these two structures joined and by transferring materials facets with lower energy facets appear, resulting in the formation of asymmetrical structure. Finally, photoluminescence measurements show the characteristic emission in the green of WZ GaP for asymmetric nanowires, even with no passivation, which confirms the good crystalline quality of our samples / Mestrado / Física / Mestre em Física
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/305734 |
| Date | 07 April 2016 |
| Creators | Silva, Bruno César da, 1988- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Cotta, Mônica Alonso, 1963-, Zagonel, Luiz Fernando, 1979-, Baptista, Daniel Lorscheitter, Cordeiro, Cristiano Monteiro de Barros |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 68 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0034 seconds