Impacto do processo de cristalização na microestrutura e na resistência à flexão de cerâmicas de silicato de lítio reforçadas por zircônia / Impact of crystallization firing process on the microstructure and flexural strength of zirconia-reinforced lithium silicate glass-ceramics

Submitted by HILTON RIQUIERI null (hilton.riquieri@terra.com.br) on 2018-01-11T19:29:07Z
No. of bitstreams: 1
Tese Impressão 11-01-18.pdf: 5465220 bytes, checksum: 6c44956d0ac81de9008cdd4833458455 (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-01-18T15:27:03Z (GMT) No. of bitstreams: 1
riquieri_h_dr_sjc.pdf: 5445301 bytes, checksum: bf194667a00b4990a467e32526c3cdb9 (MD5) / Made available in DSpace on 2018-01-18T15:27:03Z (GMT). No. of bitstreams: 1
riquieri_h_dr_sjc.pdf: 5445301 bytes, checksum: bf194667a00b4990a467e32526c3cdb9 (MD5)
Previous issue date: 2017-12-04 / O objetivo deste trabalho foi avaliar o silicato de lítio reforçado por zircônia quanto a sua microestrutura e as mesmas propriedades mecânicas em diferentes fases de cristalização. Cento e vinte amostras de discos de silicato de lítio reforçado por zircônia foram usinados de acordo com as normas ISO 6872 (12x1,2mm) para o ensaio de flexão biaxial. Foram separados em 4 grupos de acordo com a fase de cristalização. Grupo I: 30 amostras de Celtra pré cristalizado (CNC); Grupo II: 30 amostras de Celtra cristalizado (CC); Grupo III: 30 amostras de Suprinity Não Cristalizado (SNC) e Grupo IV: 30 amostras de Suprinity Cristalizado (SC). Os corpos de prova foram submetidos ao ensaio mecânico de flexão biaxial e em seguida realizadas análises qualitativas e quantitativas. Por meio microscopia eletrônica de varredura, microscopia eletrônica com emissão de campo MEV-FEG, EDS e difração de raios X (n=4), foi realizada a caracterização completa dos materiais e análise morfológica da microestrutura para todos os grupos. Para as análises estatísticas foram utilizados o módulo Weibull (m) e resistência característica (σ0). / The objective of this work was to evaluate the lithium silicate reinforced by zirconia as to its microstructure and the same mechanical properties in different phases of crystallization. One hundred and twenty samples of zirconia-reinforced lithium silicate discs were machined according to ISO 6872 (12x1,2mm) standards for the biaxial flexural test. They were separated into 4 groups according to the crystallization step. Group I: 30 samples of Pre-Crystallized Celtra (CPC); Group II: 30 samples of Crystallized Celtra (CC); Group III: 30 samples of Uncrystallized Suprinity (SNC) and Group IV: 30 samples of Crystallized Suprinity (SC). The specimens were submitted to the mechanical biaxial flexion test and qualitative and quantitative analyzes were performed. Scanning Electron Microscopy, Electron Microscopy with Field emission SEM-FEG, EDS and X-ray diffraction (n = 4) were carried out to characterize the materials and morphological analysis of the microstructure for all groups. The Weibull (m) and characteristic resistance (σ0) were used for the statistical analysis.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/152526
Date04 December 2017
CreatorsRiquieri, Hilton
ContributorsUniversidade Estadual Paulista (UNESP), Saavedra, Guilherme de Siqueira Ferreira Anzaloni [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess
Relation600

Page generated in 0.0022 seconds