This dissertation work deals with analysis of nickel hydroxide phases, their oxidation compounds, their stability and degradation mechanisms of electrochemically more active alpha phase on standard beta phase. The active material was prepared by both methods, electrodeposition and chemical precipitation. Main analysis method was Electrochemical Quartz Crystal Microbalance in combination with common analytical methods (cyclic voltammetry, potenciometry) can resolute between alpha and beta phases and quantitatively describe differences in main reaction by monitoring mass changes in the active material. Poor stability of the ?-Ni(OH)2 were improved by adding cations with valence two three and four into the structure instead of Ni atoms. The most important role plays cobalt and its hydroxide. Totally new way is to use titanium in combination with other cations. In electrolyte the most significant addition is LiOH, which has beneficial influent on cycle ability, stability in strong alkaline medium and cycle life.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:233539 |
| Date | January 2011 |
| Creators | Špičák, Petr |
| Contributors | Trnková, Libuše, Kadlec, Jaromír, Kazelle, Jiří |
| Publisher | Vysoké učení technické v Brně. Fakulta elektrotechniky a komunikačních technologií |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds