This study investigated the production of powdered activated carbon derived from carbon black of pyrolyzed waste tires, and their adsorptive capacity on vapor-phase mercury chloride (HgCl2) using both adsorption column and thermogravimetric adsorption systems. The adsorption isotherms and kinetic models were further simulated in the study. In addition, an innovative compositive impregnation process was developed to increase the sulfur content of powdered activated carbon derived from waste tires.
The activation of carbon black to form powdered activated carbon was performed in a tubular oven. The operating parameters including activation temperatures, activation time, and water feed rates were investigated in this study. Experimental results indicated that the yield of carbon-black derived powdered activated carbon (CBPAC) decreased with the increase of activation temperature, activation time, and water feed rate, while the BET surface area and pore volume decreased. In the comparison of activation time and water feed rate in the activation process, activation time had an important impact on the production of specific surface area than water feed rate. The optimal operating parameters included activation temperature of 900¢J, activation time of 180min, water feed rate of 0.5 mLH2O/gC-sec, and water injection behind activation process of 17.5 min.
From the analysis of carbon surface, the carbon contents of powdered carbon black (PCB), CBPAC, commercial powdered activated carbon (CPAC) were 89.5%, 87.6%, and 88%, respectively. The C (1s) peak region of PCB consisted of 49.8% C-C, 38.9% C-O, 10.5% C=O or O-C-O. Similar analysis results showed that the total area of the C (1s) peak region of CBPAC consisted of 57.5% C-C, 26.8% C-O, 8.1% C=O or O-C-O, and 7.6% O-C=O. Similar to CPAC, the C (1s) peak region consisted of 42.6% C-C, 41.8% C-O, and 15.6% O-C=O. Furthermore, the sulfur contents of PCB and CBPAC were both 0.5%. The S (2p) peak region of PCB consisted of 58.9% ZnS (zinc sulfide) and 41.1% S=C=S. For CBPAC, the S (2p) peak region solely contained S=C=S.
The comparison of two sulfur impregnation processes revealed that the innovative compositive impregnation process could simultaneously increased the sulfur content and the BET surface area of powdered activated carbon (PAC), however, the direct impregnation process increased the sulfur content while the BET surface area of PAC decreased linearly. Without the disadvantages of time and energy consumption associated with direct impregnation, the compositive impregnation is an efficient and energy-saving process for producing sulfurized PAC with a high BET surface area and high sulfur content.
Experimental results obtained from the adsorption column tests indicated that the influence of the adsorption depth on the adsorptive capacity of CBPAC did not vary much, while the adsorptive capacity of CBPAC increased with HgCl2 concentration. Furthermore, the adsorptive capacity of CBPAC on vapor-phase HgCl2 was less than that of CPAC at the adsorption temperatures of 25~150¢J and high humidity of 12.3 wt %. The difference of adsorptive capacity for CBPAC and CPAC correlated closely with BET surface area and sulfur content.
Results form the thermogravimetric adsorption analysis indicated that the adsorptive capacity of CBPAC and initial adsorption rate on vapor-phase HgCl2 increased with HgCl2 concentration and decreased with adsorption temperature. In the kinetic modeling, the deviation of experimental and simulated values simulated by the pseudo-first-order model was lower than those of pseudo-second-order models. Furthermore, the r (correlation coefficient) of pseudo-first-order and pseudo-second-order models were 0.9745~0.9977 and 0.9217~0.9780, respectively. It suggested that the pseudo-first-order model could simulate the adsorption of HgCl2 onto CBPAC better than pseudo-second-order model.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0324105-112349 |
| Date | 24 March 2005 |
| Creators | Lin, Hsun-Yu |
| Contributors | none, none, none, none, none, none, none, Chung-shin Yuan |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0324105-112349 |
| Rights | unrestricted, Copyright information available at source archive |
Page generated in 0.0019 seconds