New vigorous regulations have been established for decreasing the allowable formaldehyde emissions from nonstructural wood based composites. Two main sources of formaldehyde emission in non-structural wood based composites are adhesive and wood. Adhesives are quite well known and great efforts have been conducted to decrease their formaldehyde content; however formaldehyde emission from wood has received little attention and it is not completely understood. Wood-borne formaldehyde emission exists in a complex equilibrium in wood matrix. The reaction between formaldehyde and wood hydroxyl groups/water can hinder the complete formaldehyde extraction. In order to have a complete formaldehyde extraction, a stronger nucleophile than hydroxyl and water groups is needed.
In this study cross-linked poly (allylamine) (PAA) beads were synthesized and used as a strong nucleophile to extract all the biogenic and synthetic free-formaldehyde within the woody matrix of never-heated and heat-treated Virginia pines; the results were compared to simple water extraction. A new formaldehyde capturing device was also developed using a serum bottle.
Results showed that there was no advantage of using PAA beads over simple water extraction for extracting woody matrix free-formaldehyde. This means that simple water extraction can extract all the free-formaldehyde from the woody matrix. It was also found that thermal treatment resulted in generating more wood-borne formaldehyde. The other important finding was the new developed formaldehyde capturing device. The device was very promising for detecting wood-borne formaldehyde from very small pieces of wood (5-70 mg) and can be very useful in future studies. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/73511 |
| Date | 06 June 2014 |
| Creators | Tasooji, Mohammad |
| Contributors | Forest Resources and Environmental Conservation, Frazier, Charles E., Roman, Maren, Renneckar, Scott Harold |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Thesis |
| Format | ETD, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0024 seconds