This study develops and presents a friction stir weld (FSW) quality assurance tool based on control of weld zone temperature. Apart from correct tool geometry, tool tilt angle, traverse speed and forge force during welding, one important requirement is that the weld material be sufficiently plasticised (softened). The level of plasticisation is related to weld zone temperature which is primarily dependent on spindle speed, traverse speed and forge force. When all other conditions are correct, sufficiently plasticised material flows around and consolidates behind the tool without the production of voids in the weld. Typically, weld temperature varies along the weld length which may result in variations in weld quality. Weld zone temperature control makes constant weld zone temperature possible. In this study, thermocouple sensors were embedded in the FSW tool and a weld zone temperature control algorithm was developed. Spindle speed was the actuating mechanism for controlling weld temperature. The system was modelled and controllers were designed using Matlab tools. The system was simulated and the performance was compared to the system performance during welding. The control system ensures that the weld zone temperature can be maintained irrespective of the presence of thermal disturbances. Tensile testing was conducted which confirmed a range of temperature in which the welds resulted in consistent strength.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:26656 |
Date | January 2015 |
Creators | Pothier, Raymond Peter |
Publisher | Nelson Mandela Metropolitan University, Faculty of Engineering, the Built Environment and Information Technology |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis, Masters, MEngineering |
Format | xvi, 128 leaves, pdf |
Rights | Nelson Mandela Metropolitan University |
Page generated in 0.0018 seconds