Soldagem circunferencial do aço inoxidável super duplex UNS S32750 pelo processo MIG com controle CMT® / Circunferencial welding aplied for inox steel super duplex UNS S32750 using the process MIG using CMT&reg control

Neste trabalho foram realizados experimentos de soldagem circunferencial em tubos de aço inoxidável super duplex UNS S32750, com diâmetros de 19,05 mm e 48,20 mm. Foram executadas soldas utilizando-se diversos parâmetros de soldagem num equipamento MIG com controle CMT&reg Cold Metal Transfer. Os cordões de solda foram avaliados por inspeção visual e dimensional, além dos ensaios de tração e microdureza Vickers, bem como a análise microestrutural em conjunto com análise de precipitação de fases, a qual foi realizada em acordo com a prática A da norma ASTM A923, e ensaio de corrosão conforme a prática A da norma ASTM G48 em conjunto com a norma ASTM A923. Os resultados indicaram que a soldagem do tubo com diâmetro de 19,05 mm apresentou cordão de solda com dimensões inaceitáveis conforme norma, tendo sido esta condição atribuída a utilização de um elevado diâmetro do arame para as condições (parâmetros) usadas de soldagem. A soldagem do tubo com diâmetro de 48,20 mm apresentou falta de penetração nas condições empregadas, quando soldado pelo processo CMT&reg convencional. No caso da utilização do CMT&reg combinado com arco pulsado, em condições que geraram maior aporte de calor durante a soldagem, assim obteve-se penetração total da junta e acabamento superficial adequado. Os resultados indicaram que a soldagem utilizando o processo CMT&reg combinado com arco pulsado, nas condições (parâmetros) empregados geraram bom acabamento superficial, aliado propriedades mecânicas compatíveis, atendendo exigências de normas, bem como uma microestrutura balanceada e alta resistência à corrosão. / This study carried out circumferential welding experiments in UNS S32750 Super Duplex Stainless Steel tubes using diameters of 19,05 mm and 48,20 mm. Welds were performed using various welding parameters on a MIG machine with Cold Metal Transfer&reg CMT control. The weld joints were evaluated by visual and dimensional inspection in addition to the Vickers microhardness and traction tests, as well as the microstructural analysis in conjunction with phase precipitation analysis, which was performed according to practice A of ASTM A923, and corrosion test in accordance with practice A of ASTM G48 in conjunction with ASTM A923. The results indicated that welds performed in pipes with a diameter of 19.05 mm showed a weld joint with unacceptable dimensions according to the standard, this condition being attributed the use of a high wire diameter for the welding conditions used. Welding performed for pipes with a diameter of 48.20 mm showed a lack of penetration under the conditions employed when welded by the conventional CMT&reg process. In the case of the use of CMT&reg combined with pulsed arc, under conditions that generated greater heat input during welding, this resulted in total penetration of the joint and adequate surface finish. The results indicated that welding using the CMT&reg process combined with pulsed arc, under the conditions (parameters) employed generated good surface finish, combined mechanical properties, meeting standards requirements, as well as a balanced microstructure and high resistance to corrosion.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-23052017-152804
Date29 March 2017
CreatorsInvernizzi, Bruno Pizol
ContributorsNeves, Maurício David Martins das
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0023 seconds