<p>The goal of this work has been to evaluate the different experimental techniques used for quantitative analysis of multi-phase materials systems. </p><p>Powder based specimens containing two-phases, austenite and ferrite , were fabricated and quantified. The volume fraction of ferrite varied from 2 Vol% to 50 Vol%. </p><p>X ray powder diffraction (XRD) measurements were based on two peak analysis. Computer based software Topas was used for quantitative analysis, which is believed to be the most advanced in this field. XRD results were found within the absolute limit of +/- 4% of given ferrite volume fraction. Volume fraction as low as 2 Vol% was successfully detected and quantified using XRD. However, high statistical error was observed in case of low volume fraction, such as 2 Vol% and 5 Vol% ferrite volume fraction. </p><p>Magnetic balance (MB) measurements were performed to determine the volume fraction of magnetic phase, ferrite. MB results were found in good agreement with given volume fractions. As low as 2 Vol% volume fraction was detected and quantified with MB. MB results were within the absolute limit of +/- 4% of given ferrite volume fraction. </p><p>Image analysis (IA) was performed after proper sample preparation as required by electron backscatter diffraction (EBSD) mode of Scanning electron microscopy (SEM). IM results were found within the absolute limit of +/- 2 % of given ferrite volume fraction. However, high statistical error was observed in case of 2 Vol% volume fraction.</p>
| Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:liu-2681 |
| Date | January 2004 |
| Creators | Fawad, Salman Kohar |
| Publisher | Linköping University, The Department of Physics, Chemistry and Biology, Institutionen för fysik, kemi och biologi |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, text |
Page generated in 0.0019 seconds