Cellulose nanofibrils are a biobased and renewable material with potential to be used in many different applications. Such applications include air filtration, absorption of liquids, and thermal insulation. To be used for these applications the cellulose nanofibrils must form a porous and dry material. However, maintaining some degree of porosity after drying is difficult, since the fibrils are extracted in liquid and tend to collapse into a dense material upon drying. Certain methods have proven effective for making a dry porous material from cellulose nanofibrils, but these are often expensive and not suitable for large scale production. The aim of this project is to test possible methods for making a highly porous cellulose nanofibril-based material. These methods must be environmentally sustainable and suitable for large scale production. An extensive screening has been conducted with the aim of identifying methods resulting in materials with high porosity. The obtained materials have been analysed further to give a more thorough understanding of the porosity as well as other characteristics. The results indicate that cross-links in the material strengthen the structure, and that drying samples from water always results in complete collapse or very dense materials while drying samples from certain solvents other than water results in more porous materials. The analysed materials had very different porosities, some of which were relatively high. The most porous material analysed by Brunauer-Emmett-Teller gas adsorption had a surface area of 9.5 m2/g. This project gives insight into how cross-linking chemistries and treatment with different solvents and pH affect the resulting cellulose nanofibril-based material, as well as knowledge about which methods can be used to successfully produce dry porous cellulose nanofibril-based materials.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-179266 |
Date | January 2021 |
Creators | Törneman, Hedda |
Publisher | Linköpings universitet, Institutionen för fysik, kemi och biologi |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds