In this master thesis project, attempts were made to synthesize, pore size tailor, and characterize ZIF-8 and several mixed-linker ZIF structures to improve capture of the greenhouse gasses CH4, CO2, and SF6. Three experimental linkers, 2-methylbenzimidazole, 2-aminobenzimidazole, and 5-nitrobenzimidazole were chosen to gradually substitute 2-methylimidazole as the linker in ZIF-8. This substitution was intended to gradually reduce pore sizes and possibly adding functionality to the apertures present in ZIF-8 (three different series). The methods of synthesis were first evaluated by performance and modified. Three series of ZIF-hybrids were then synthesized and characterized using PXRD, FTIR, 1HNMR, SEM, extensive sorption measurements, and subsequent modeling to evaluate any success tailoring the hybrid ZIF apertures to increase gas sorption. After modifying synthesis conditions, the undertaking was deemed a success as all three linkers were possible to incorporate to some degree. Hybrid ZIFs were mostly XRD-crystalline. The cleaning process was deemed sufficient. Linker incorporation was not complete but increased with the added linker. Sodalite topology was confirmed in ZIF-8 samples and confirmed as modified in hybrid ZIFs. The hybrid ZIFs did indeed show altered sorption results and surprisingly promising results regarding gas selectivity (favoring sorption of one gas over that of another).
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-434657 |
| Date | January 2021 |
| Creators | Hedbom, Daniel |
| Publisher | Uppsala universitet, Nanoteknologi och funktionella material |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | UPTEC K, 1650-8297 ; 20040 |
Page generated in 0.002 seconds