This thesis is about the phase transformation, shape, size distribution and coalescence of TiO2 (part I) and ZrO2 (part II) nanopartilces produced by Nd-YAG laser ablation on metal targets under oxygen background gas, and characterized by analytical electron microscopy. The optimum laser ablation condition that satisfactory and routinely yield high-pressure phases of TiO2 (i.e. £\-PbO2-type and fluorite-related structures) and ZrO2 with high residual stress were reported. Part I-1 focuses on physical coagulation, by Van der Waals force, of the TiO2 condensates at temperatures up to about 1000 K as a result of post-condensation radiant heating. In part I-2, imperfect oriented attachment of nanoparticles over specific surfaces is rationalized to cause accretion and defects for the rutile condensates. Brownian motion may proceed above a critical temperature for anchorage release at the interface of imperfect attached nanoparticles until an epitaxial relationship is reached. Part I-3 deals with further the Brownian-type rotation of the imperfectly impinged £\-PbO2-type TiO2 and rutile nanocondensates until interfacial-energy cusp was reached. In part I-4 laser ablation condensation synthesis of dense TiO2 polymorphs and their phase transformations were documented. Part II-1 is about dense tetragonal (t)-ZrO2 and cubic (c-) nanocondensates which were synthesized under very rapid heating and cooling by pulsed Nd-YAG laser ablation with oxygen background gas. The t-ZrO2 nanoparticles were found to form deformation twins/faults and followed unique transformation path upon local electron dosage. Electron diffraction indicated that the dense c- and t- phase with specific size and residual stress were allowed to relax and/or kinetically phase change into lower-energy state as constrained by the intersections of the internal energy vs. cell volume plots calculated for the two polymorphs (Part II-2).
Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0712105-104244 |
Date | 12 July 2005 |
Creators | Tsai, Meng-Hsiu |
Contributors | Gan, Der shin, Chen, Shueiyuan, Hsieh, Ker-Chang, Hwang, S.L., Shen, Pouyan, Kao Po-We |
Publisher | NSYSU |
Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
Language | English |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0712105-104244 |
Rights | not_available, Copyright information available at source archive |
Page generated in 0.002 seconds