The influence of various pressure-less heating schedules (CRH - Constant Rate of Heating, TSS - Two Step Sintering, RCS – Rate Controlled Sintering) on the final microstructure of cubic zirconia ceramics was studied in this master´s thesis. There were used nanopowders ZrO2 (stabilized with 8 mol.% Y2O3) with initial particle size 80 nm (TZ-8Y) and 140 nm (TZ-8YSB). Powders were cold isostatically pressed and pressure-less sintered in air by different heating regimes. It was found that for both studied materials the modification of conventional sintering (CRH) using lower sintering temperatures and longer sintering dwell times can result in samples with finer microstructure. For example, the sintering of TZ-8YSB ceramics at a relatively low temperature (1270 °C) but for very long time (60 h) led to ceramics with the same final density (99,25 % of theoretical density) and almost identical grains (1,31 m vs. 1,27 m) in compare with TSS (1440 °C/ 1290 °C/ 15 h). On the other hand, RCS method showed no positive effect on the microstructure of both materials in comparison with CRH method. The obtained results indicate that the microstructure of c-ZrO2 ceramics can be influenced rather in its third sintering stage (by CRH and TSS methods) than in the second sintering stage (by RCS method).
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:230343 |
| Date | January 2012 |
| Creators | Stromský, Tomáš |
| Contributors | Hadraba, Hynek, Maca, Karel |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0016 seconds