This thesis investigates the chemistry of ammonia borane (NH3BH3) relevant to the development of hydrogen storage systems for vehicular applications. Because of its high hydrogen content and low molecular weight ammonia borane has the potential to meet stringent gravimetric hydrogen storage targets of gt;9 wt%. Two of the three moles of H2 in ammonia borane can be released under relatively mild conditions, with the highest gravimetric yield obtained in the solid-state. However, ammonia borane does not deliver sufficient H2 at practical temperatures and the products formed upon H2 loss are not amenable to regeneration back to the parent compound. The literature synthesis of ammonia borane was modified to facilitate large scale synthesis, and the deuterated analogues ND3BH3 and NH3BD3 were prepared for the purpose of mechanistic studies. The effect of lithium amide on the kinetics of dehydrogenation of ammonia borane was assessed by means of solid-state reaction in a series of specific molar ratios. Upon mixing lithium amide and ammonia borane, an exothermic reaction ensued resulting in the formation of a weakly bound adduct with an H2N...BH3-NH3 environment. Thermal decomposition at or above temperatures of 50eg;C of this phase was shown to liberate gt;9 wt% H2. The mechanism of hydrogen evolution was investigated by means of reacting lithium amide and deuterated ammonia borane isotopologues, followed by analysis of the isotopic composition of evolved gaseous products by mass spectrometry. From these results, an intermolecular multi-step reaction mechanism was proposed, with the rates of the first stage strongly dependent on the concentration of lithium amide present. Compounds exhibiting a BN3 environment (identified by means of solid-state sup1;sup1;B NMR spectroscopy) were formed during the first stage, and subsequently cross link to form a non-volatile solid. Further heating of this non-volatile solid phase ultimately resulted in the formation of crystalline Li3BN2 - identified by means of powder X-ray diffractometry. This compound has been identified as a potential hydrogen storage material due to its lightweight and theoretically high hydrogen content. It may also be amenable to hydrogen re-absorption. The LiNH2/CH3NH2BH3 system was also investigated. Thermal decomposition occurred through the same mechanism described for the LiNH2/NH3BH3 system to theoretically evolve gt;8 wt% hydrogen. The gases evolved on thermal decomposition were predominantly H2 with traces of methane detected by mass spectrometry.
| Identifer | oai:union.ndltd.org:ADTP/238187 |
| Date | January 2008 |
| Creators | Benge, Kathryn Ruth |
| Publisher | The University of Waikato |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://www.waikato.ac.nz/library/research_commons/rc_about.shtml#copyright |
Page generated in 0.0018 seconds