Yes / Owing to their small size, good wettability, uniform dispersion ability and high thermal properties, the nickel-plated carbon nanotubes (Ni-CNTs) with different aspect ratios are used to reinforce reactive powder concrete (RPC) through modifying the nano/micro- structural units of concrete. Incorporating only 0.075 vol% of Ni-CNTs (0.03 vol% of CNTs) can significantly increase mechanical properties of RPC. The enhancement effect on compressive strength caused by the incorporation of Ni-CNTs with aspect ratio of 1000 reaches 26.8%/23.0 MPa, mainly benefiting from the high polymerization C-S-H gels, low porosity, and refined pore structure. The 33.5%/1.92 MPa increases of flexural strength can be attributed to the decrease of large pore, original cracks, molar ratio of CaO to SiO2, and gel water content when Ni-CNTs with aspect ratio of 125 are added. Ni-CNTs with aspect ratio of 1500 have the largest utilization rate of being pulled-out, resulting from the improvement of dispersibility and the pining effect of nickel coating and then leading to the increased toughness. Therefore, incorporating Ni-CNTs can fundamentally modify the nano/micro- scale structural nature of RPC, providing a bottom-up approach for controlling the properties of RPC. / Funding supported from the National Science Foundation of China (51908103 and 51978127) and the China Postdoctoral Science Foundation (2019M651116).
| Identifer | oai:union.ndltd.org:BRADFORD/oai:bradscholars.brad.ac.uk:10454/18205 |
| Date | 28 November 2020 |
| Creators | Dong, S., Wang, D., Ashour, Ashraf, Han, B., Ou, J. |
| Publisher | Elsevier |
| Source Sets | Bradford Scholars |
| Language | English |
| Detected Language | English |
| Type | Article, Accepted manuscript |
| Rights | © 2020 Elsevier. Reproduced in accordance with the publisher's self-archiving policy. This manuscript version is made available under the CC-BY-NC-ND 4.0 license. |
Page generated in 0.0017 seconds