The studied material is an A356 Al alloy, used to produce engine cylinder heads for the automotive industry by die casting process. The material displays a quite coarse dendritic microstructure in a eutectic matrix, with a mean grains size of 25 microns, intemetallic precipitates and porosities. The tensile properties are strongly affected by testing temperature, with a quite sensitive drop of the Young's modulus, the Yield stress as the temperature was raised. The isothermal fatigue life dropped of markedly (approximately 10 times) when the testing temperature is raised from 120 to 280 °C, under strain control. From the themomechanical in-phase cyclic tests, with temperature varying from (120 to 280 oC), it was possible to observe that life is quite similar to the isothermal fatigue test at 280 oC. In this case, the more sensitive damage caused the in-phase mechanical and thermal cycle take place at the highest temperature. Relaxation tests indicated two distinct behaviors, with the temperature of 240°C being a threshold. At lower temperatures, the material hardens cyclically whereas it softens cyclically at higher temperatures. From the fatigue crack growth results, it was observed that temperature and wave shape has a strong influence on the crack growth rate as well as on the stress intensity threshold. Considering sinusoidal wave shape (10 Hz), as the temperature increased the DKth decreased and the crack propagation rate increased. However, the rate as da/dN change with temperature is quite similar, as an indicative that the micromechanism of crack growth has not changed due to the high frequency used, and it was due only to loss of mechanical strength. An elastic-visco-plastic non-isothermal constitutive law was identified for the material. For the cast material studied in this work, the mechanical behavior parameters are statistically distributed. However, it was shown that the model was able to reproduce, with a reasonable approximation, the stress - strain relationship at different temperatures, for the isothermal and anisothermal cases.
| Identifer | oai:union.ndltd.org:CCSD/oai:tel.archives-ouvertes.fr:tel-00661622 |
| Date | 27 April 2011 |
| Creators | Angeloni, Mauricio |
| Publisher | École normale supérieure de Cachan - ENS Cachan |
| Source Sets | CCSD theses-EN-ligne, France |
| Language | English |
| Detected Language | English |
| Type | PhD thesis |
Page generated in 0.0022 seconds