Surface chemistry of a Cu(I) beta-diketonate precursor and the atomic layer deposition of Cu2O on SiO2 studied by x-ray photoelectron spectroscopy

This article has been published online on 21st May 2014, in Journal of Vacuum Science & Technology A: Vac (Vol.32, Issue 4):
http://scitation.aip.org/content/avs/journal/jvsta/32/4/10.1116/1.4878815?aemail=author

DOI: 10.1116/1.4878815

This article may be accessed via the issue's table of contents at this link:
http://scitation.aip.org/content/avs/journal/jvsta/32/4?aemail=author

The surface chemistry of the bis(tri-n-butylphosphane) copper(I) acetylacetonate, [(nBu3P)2Cu(acac)], and the thermal atomic layer deposition (ALD) of Cu2O using this Cu precursor as reactant and wet oxygen as co-reactant on SiO2 substrates are studied by in-situ X-ray photoelectron spectroscopy (XPS). The Cu precursor was evaporated and exposed to the substrates kept at temperatures between 22 °C and 300 °C. The measured phosphorus and carbon concentration on the substrates indicated that most of the [nBu3P] ligands were released either in the gas phase or during adsorption. No disproportionation was observed for the Cu precursor in the temperature range between 22 °C and 145 °C. However, disproportionation of the Cu precursor was observed at 200 °C, since C/Cu concentration ratio decreased and substantial amounts of metallic Cu were present on the substrate. The amount of metallic Cu increased, when the substrate was kept at 300 °C, indicating stronger disproportionation of the Cu precursor. Hence, the upper limit for the ALD of Cu2O from this precursor lies in the temperature range between 145 °C and 200 °C, as the precursor must not alter its chemical and physical state after chemisorption on the substrate. 500 ALD cycles with the probed Cu precursor and wet O2 as co reactant were carried out on SiO2 at 145 °C. After ALD, in situ XPS analysis confirmed the presence of Cu2O on the substrate. Ex-situ spectroscopic ellipsometry indicated an average film thickness of 2.5 nm of Cu2O deposited with a growth per cycle of 0.05 Å/cycle. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) investigations depicted a homogeneous, fine, and granular morphology of the Cu2O ALD film on SiO2. AFM investigations suggest that the deposited Cu2O film is continuous on the SiO2 substrate.

Identiferoai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:20074
Date January 2014
CreatorsDhakal, Dileep, Waechtler, Thomas, E. Schulz, Stefan, Gessner, Thomas, Lang, Heinrich, Mothes, Robert, Tuchscherer, Andre
ContributorsFraunhofer ENAS
PublisherTechnische Universität Chemnitz
Source SetsHochschulschriftenserver (HSSS) der SLUB Dresden
LanguageEnglish
Detected LanguageEnglish
Typedoc-type:article, info:eu-repo/semantics/article, doc-type:Text
Sourcehttp://scitation.aip.org/content/avs/journal/jvsta/32/4/10.1116/1.4878815?aemail=author
Rightsinfo:eu-repo/semantics/openAccess
Relation10.1116/1.4878815

Page generated in 0.0017 seconds