We present a colloidal synthesis of quaternary Cu–Zn–In–S (CZIS) nanoplatelets (NPLs) by means of partial cation exchange. Starting with the synthesis of highly monodisperse binary CuS NPLs with lateral dimensions of ∼64 nm and thickness of ∼5 nm, we further performed a cation exchange reaction in which copper was partly replaced by indium, leading to Cu–In–S NPLs. To enhance the stability of the resulting NPLs and to improve their optical properties, we carried out the ZnS shell growth via both the heterogeneous nucleation of ZnS on the NPLs and via partial cation exchange on the surface of the particles. The latter reaction resulted, however, in rather an alloyed than the core/shell structure, whereas the reaction between zinc and sulfur precursors yielded unusual cookie-like hexagonal shaped structure, in which ZnS trigonal extensions grew only on one of the basal planes of the plates along the thickness direction. Upon ZnS growth, the lateral dimensions of the resulting core/shell CZIS/ZnS and alloyed CZIS NPLs distinctly increased to ∼80 and ∼75 nm, respectively. The analysis of the optical properties of the alloyed CZIS NPLs showed photoluminescence (PL) in the range from 780 to 820 nm depending on the reaction time and temperature. This PL signal originated mainly from small nanoparticles formed as a byproduct in the synthesis. In contrast to the alloyed NPLs, PL measurements of the core/shell CZIS/ZnS platelets showed a weak emission in the near-infrared region (PL maximum at approx. 1110 nm), which so far has rarely been reported for the copper chalcogenide-based two-dimensional structures.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:74324 |
| Date | 01 April 2021 |
| Creators | Lox, Josephine F. L., Dang, Zhiya, Lê Anh, Mai, Hollinger, Eileen, Lesnyak, Vladimir |
| Publisher | American Chemical Association |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/acceptedVersion, doc-type:article, info:eu-repo/semantics/article, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 1520-5002, 10.1021/acs.chemmater.9b00005, info:eu-repo/grantAgreement/European Commission/H2020 | RIA/779373//Micro Quantum Dot-Light Emitting Diode and Organic Light Emitting Diode Direct Patterning/MiLEDI, info:eu-repo/grantAgreement/European Commission/FP7 | SP2 | ERC/614897//Advancing the Study of Chemical, Structural and Surface Transformations in Colloidal Nanocrystals/TRANS-NANO |
Page generated in 0.0024 seconds