Previous issue date: 2017-04-25 / O presente trabalho tem o objetivo de desenvolver novos materiais cerâmicos refratários, através do aproveitamento de resíduos derivados da geração de energia elétrica a partir da queima da casca de arroz. Microfibras cerâmicas foram introduzidas com o intuito de melhorar a resistência ao choque térmico. Os corpos de prova foram produzidos pelo método de prensagem uniaxial (20MPa), com substituição da argila refratária por sílica da casca de arroz (20%), e microfibras cerâmicas (20%) ou fibras de aço (1,9%, 3,8% e 5,6%). A sinterização ocorreu na temperatura de 1300º C. As propriedades físicas foram avaliadas através dos ensaios de porosidade aparente, absorção de água, densidade de massa, retração linear de queima, variação de massa e condutividade térmica. As propriedades mecânicas foram avaliadas pelos ensaios de resistência à compressão e resistência à flexão em três pontos. As propriedades térmicas foram avaliadas pelo ensaio de resistência ao choque térmico. As análises de XRD mostraram que houve transformação de parte da sílica presente na mistura em mulita e o restante permaneceu como quartzo. Além disso, a adição de sílica de casca de arroz resultou em uma microestrutura com baixa porosidade, alta retração de queima e elevada resistência mecânica. As cerâmicas com fibras apresentaram porosidade elevada, menor retração de queima e menor condutividade térmica do que a cerâmica de referência. Relativamente à resistência ao choque térmico, as cerâmicas com fibras de aço apresentaram desempenho significativamente superior em relação às cerâmicas sem fibras. / This study aims to develop new refractory ceramic materials, through the use of waste resulting from the electricity generation from rice husk burning. Ceramic microfibers were introduced with the aim of improving the resistance to thermal shock. The samples are produced by uniaxial pressing method (20MPa), by replacing refractory clay for ashes of rice husks (20%), ceramic microfibers (20%), and steel fiber (1,8%, 3,8% and 5,6%). The sintered occurred at temperature of 1300º C. Samples physical properties will be evaluated through the apparent mass density tests, apparent porosity, water absorption, linear shrinkage after burning, mass variation and thermal conductivity. The mechanical properties are evaluated by the compressive strength test and three points flexural test. The thermal properties will be evaluated by the thermal shock resistance test. XRD analyzes showed that some silica was present in the mullite mixture and the rest remained as quartz. The results show that the addition of SCA resulted in a microstructure with low porosity and with high firing shrinkage. The ceramics with fibers presented high porosity and low firing shrinkage and thermal conductivity, even, lower than the reference ceramic. The ceramics with SCA presented high mechanical resistance, while the ceramics with steel fibers had more ductile behavior. Regarding the thermal shock resistance, the ceramics with steel fibers presented a significantly superior performance in relation to the ceramics without fibers.
| Identifer | oai:union.ndltd.org:IBICT/oai:10.1.0.46:riu/1950 |
| Date | 25 April 2017 |
| Creators | Nunes, Alessandro da Silva |
| Contributors | Tier, Marco Antônio Durlo, Marangon, Ederli |
| Publisher | Universidade Federal do Pampa, Mestrado Acadêmico em Engenharia, UNIPAMPA, Brasil, Campus Alegrete |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNIPAMPA, instname:Universidade Federal do Pampa, instacron:UNIPAMPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds