Previous issue date: 2013-02 / Membranas compostas de osmose inversa (OI) comerciais (BW30-Dow Filmtec) foram modificadas através do recobrimento com membrana de poli(álcool vinílico) (PVA) reticulado com glutaraldeído (GA) e membrana compósita contendo carvão ativado em pó (CAP) em matriz de PVA para aumento de sua resistência ao cloro. Esse estudo compara o desempenho da membrana comercial original e as modificadas em meio oxidante de cloro (NaClO 300 mg/L, NaCl 2,000 mg/L, pH 9.5). O tempo de exposição e a concentração do cloro foram monitorados em termos de ppm.h (concentração da solução de cloro em ppm exposta a membrana por um tempo fixo em h). Análises de ATR-FTIR e TGA confirmaram a reação de reticulação entre o GA e o PVA além da influência do CAP na matriz da membrana compósita de PVA. Imagens do MEV relativas às membranas original e modificada foram empregadas para avaliação do cobrimento da superfície das membranas. A rejeição salina (NaCl) e a permeabilidade hidráulica foram avaliadas durante um período maior que 100 h. Ambas as modificações de superfície demonstraram com eficiência o aumento da resistência ao cloro da membrana comercial de OI de 1,00 ppm.h para mais de 15.000 ppm.h. / Commercial thin-film composite reverse osmosis (RO) membranes (BW30-Dow Filmtec) were modified by covering it with a poly(vinyl alcohol) (PVA) membrane crosslinked with glutaraldehyde (GA) and a composite membrane containing powdered activated carbon (PAC) in a matrix of PVA to improve its resistance to chlorine. This study compares the performance of the original commercial membrane and the modified ones in an oxidant chlorine medium (NaClO 300 mg/L, NaCl 2,000 mg/L, pH 9.5). The exposure time and the chlorine concentration were monitored and taken in terms of ppm.h (ppm chlorine concentration solution exposed to membrane for a fixed time in h). ATR-FTIR and TGA analysis confirmed the crosslinking reaction between GA and PVA besides the influence of PAC in the PVA matrix of the composite membrane. SEM images of the original and modified membranes were used to evaluate the surface coating of the membranes. The salt rejection (NaCl) and water permeability were measured during more than 100 h period. Both surface modifications have effectively demonstrated the increase for the chlorine resistance of the commercial RO membrane from 1,000 ppm.h to more than 15.000 ppm.h.
| Identifer | oai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/2027 |
| Date | 02 1900 |
| Creators | Silva, Lucinda Fernandes da, Instituto de Engenharia Nuclear |
| Contributors | Mendes, Luis Cláudio, Dias, Marcos Lopes, Ferraz , Helen Conceição, Borges, Criatiano Piacsek, Michel, Ricardo Cunha |
| Publisher | Instituto de Engenharia Nuclear, Programa de Pós-Graduação em Macromoléculas e Tecnologia de Polímeros, IEN, Brasil, Universidade Federal do Rio de Janeiro |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds