Previous issue date: 2012 / Este trabalho descreve o processamento de um concentrado de zirconita via fusão
com hidróxido de sódio. O objetivo foi produzir uma solução de sulfato de zirconila
(ZrOSO4). Os efeitos da razão mássica NaOH/ZrSiO4, da temperatura e do tempo de
reação foram investigados. A massa fundida foi lixiviada com água pura, seguido por
lixiviação do material insolúvel com ácido sulfúrico. Os efeitos da razão líquido/sólido
e da temperatura na lixiviação com água foram investigados, bem como a influência da
temperatura e concentração de ácido na pureza do sulfato de zirconila. As melhores
condições de fusão foram: relação mássica NaOH/ZrSiO4, (1,5/1); temperatura, 575oC e
tempo de reação, 30 min. A lixiviação com água foi mais bem conduzida com uma
razão mássica H2O/massa fundida de 5:1 a 25oC. A lixiviação ácida requer 100 mL de
ácido sulfúrico 3 mol L-1 para dissolver a massa hidratada insolúvel em água a
temperatura de 25oC. Nestas condições foram decompostos 97% em massa do
concentrado de zirconita e ao redor de 91% em massa de zircônio foi recuperado no
produto final. / This work describes the processing of a Brazilian zircon (ZrSiO4) concentrate via
fusion with sodium hydroxide. The goal was to produce a zirconyl sulphate solution
(ZrOSO4). The effects of NaOH/ZrSiO4 mass ratio, temperature and reaction time were
investigated. The fused mass was leached with pure water, followed by leaching of the
insoluble matter with sulfuric acid. The effects of temperature and liquid/solid ratio on
water leaching were investigated, as well as the influence of temperature and acid
concentration on ZrOSO4 purity. The best fusion conditions were: NaOH/ZrSiO4 mass
ratio = 1.5:1; temperature, 575oC; reaction time, 30 min. Water leaching was best
conducted with a water/fused mass ratio = 5/1 at 25oC. Acid leaching required 100 mL 3
mol L-1 H2SO4 to dissolve the water-insoluble solid at 25oC. 97 wt. % of ZrSiO4 was
decomposed and around 91 wt. % of Zr was recovered in the final product.
| Identifer | oai:union.ndltd.org:IBICT/oai:carpedien.ien.gov.br:ien/809 |
| Date | 08 1900 |
| Creators | SILVA, Reginaldo José Farias da |
| Contributors | AFONSO, Julio Carlos, GOMES, José Antonio da Cunha Ponciano, TOREM, Mauricio Leonardo, CARVALHO, Roberto José de, DUTRA, Achilles Junqueira Bourdot |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Repositório Institucional do IEN, instname:Instituto de Engenharia Nuclear, instacron:IEN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds