Orientadora : Profª. Drª. Marienne do Rocio de Mello Maron da Costa / Co-orientador : Prof. Dr. Isac José da Silva / Dissertação (mestrado) - Universidade Federal do Paraná, Setor de Tecnologia, Programa de Pós-Graduação em Construção Civil. Defesa: Curitiba, 03/06/2014 / Inclui referências / Area de concentração : Materiais e estrutura / Resumo: As argamassas colantes utilizadas para o assentamento de revestimentos ceramicos em pisos e paredes sao compostas de ligante, agregado com dimensao maxima . 0,6 mm e sao modificadas com polimeros celulosicos e vinilicos que tem finalidade de alterar a fase aquosa da argamassa e interagir na hidratacao do cimento, modificando assim as propriedades das argamassas nos estados fresco e endurecido. A norma brasileira NBR 14081-4 (2012) determina a resistencia de aderencia das argamassas colantes submetidas a diferentes tipos de cura (ao ar, submersa e termica), porem na literatura existe uma lacuna do conhecimento ainda a ser preenchida no que se refere ao impacto da cura termica no desempenho dessas argamassas. Dessa forma, este estudo teve como objetivo avaliar o efeito da cura termica segundo a NBR 14081-4 (2012) na resistencia de aderencia de argamassas colantes formuladas e caracterizadas em laboratorio com teores variados de aditivos polimericos e de cimento. Para tanto, o programa experimental dividiu o trabalho em tres etapas. A primeira etapa consistiu na avaliacao da influencia de quatro diferentes teores de cimento portland (25; 30; 35 e 40% em relacao a massa total dos solidos) no desempenho das argamassas, com teores constantes dos aditivos polimericos (HPMC e VAE). Na segunda etapa, com base nas avaliacoes da etapa anterior, foram avaliados quatro teores de cada aditivo (HPMC e VAE) e fixados dois teores de cimento (25 e 35%). Por fim, na terceira etapa o trabalho consistiu em realizar a avaliacao da microestrutura, onde foram aplicadas analises de DRX e MEV nas pastas de argamassas, para melhor entender o efeito da temperatura na estrutura mineralogica das argamassas. Os resultados mostraram que, o cimento e fundamental no aumento da resistencia de aderencia mediante a cura termica, porem foi tambem observado que a temperatura provoca degradacao da etringita na estrutura interna da pasta cimenticia. Com isso, notou-se que o polimero VAE passa a ser o maior responsavel pela resistencia de aderencia de argamassas colantes sob o impacto da cura termica. Com os dados obtidos, esse trabalho vem tambem contribuir para o meio tecnico e fabricantes de argamassas colantes, no desenvolvimento de formulacoes de argamassas colantes.
Palavras-Chave: Argamassas colantes, resistencia de aderencia, cura termica. / Abstract: Adhesive mortars used for laying floor and wall tiles are composed of binder (cement), with a maximum aggregate size is . 0.6 mm, and modified by cellulose and vinylic polymers, which is intended to provide changes in the aqueous phase and interact with the polymer mortar cement hydration process thus modifying the properties of mortars in fresh and hardened state. The NBR 14081-4 (2012) specifies the determination of the adhesion strength of adhesive mortars under different curing type (air, underwater and thermal), but there is a gap in the literature of knowledge yet to be exploited as regards the impact of thermal curing performance of adhesive mortars. Thus, this study aimed to evaluate the effect of thermal curing according to NBR 14081-4 (2012) on the bond strength of adhesive mortars formulated and characterized in the laboratory with varying amounts of polymeric additives and cement. For the study, the experimental design was divided into three steps. The first step was to evaluate the influence of the Portland cement in the performance of adhesive mortars, they were formulated from four cement contents was: 25; 30; 35 and 40% (on the total weight of solids) with content constant of polymeric additives (HPMC and VAE). In the second step, two amount of cement (25 and 35%) were selected based on reviews of the first stage, to evaluate four amount of each additive (HPMC and VAE) in order to verify the effect of these additives on the performance of adhesive mortars. Finally, the third step consisted of performing the work in a microstructure evaluation, where XRD and SEM were applied to the pastes of mortars, to better understand the effect of temperature on the mineralogical of mortars. The results showed, that the cement content was essential to obtain higher adhesion strength by thermal curing, nevertheless, it was observed that the effect of temperature causing degradation of the ettringite on cement mineralogy. However, it was noted that the vinyl additive VAE becomes the most responsible for the mortars do not lose bond strength on the impact of temperature (70‹C). With the data obtained, this work contributes to the technical means and manufacturers of adhesives mortars, developing formulations of adhesive mortars.
Keywords: adhesive mortars, adhesion strength, thermal curing.
| Identifer | oai:union.ndltd.org:IBICT/oai:dspace.c3sl.ufpr.br:1884/37371 |
| Date | January 2014 |
| Creators | Kotoviezy, Leidimara Aparecida Martins |
| Contributors | Costa, Marienne do Rocio de Mello Maron da, Silva, Isac José da, Universidade Federal do Paraná. Setor de Tecnologia. Programa de Pós-Graduação em Engenharia de Construção Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 120p. : il. algumas color., tabs., application/pdf |
| Source | reponame:Repositório Institucional da UFPR, instname:Universidade Federal do Paraná, instacron:UFPR |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Disponível em formato digital |
Page generated in 0.0022 seconds